Temperature Stability and Chemical Compatibility of Novel Li1.6Zn1.6Sn2.8O8 Ceramics

Xiaolei Shi,Huaiwu Zhang,Dainan Zhang,Fang Xu,Gang Wang,Yuhang Zheng,Cheng Liu,Jie Li,Lichuan Jin,Lijun Jia

DOI: https://doi.org/10.1016/j.matchemphys.2019.121960

IF: 4.778

2019-01-01

Materials Chemistry and Physics

Abstract:A new Li1.6Zn1.6Sn2.8O8 (LZS) ceramic with good temperature stability was synthesized by a simple solid-state reaction. The LZS ceramic exhibited nearly compact structure and possessed optimum dielectric characteristics of epsilon(r) = 11.24, Qxf = 59800 GHz, tau(f )= - 7.86 ppm/degrees C. The influences of Li2O-B2O3-SiO2-CaO-Al2O3 (LBSCA) glass additive on the microwave dielectric characteristics, structure composition and morphology of LZS ceramics were investigated. The results demonstrated that LBSCA glass could significantly reduce sintering temperature and then suppress the appearance of impure phase SnO2. The scanning electron microscope (SEM) results indicated that the microstructure evolution from flake-like to particle-like appeared with increasing LBSCA, which was accompanied by the decline in grain sizes from 2.66 mu m to 0.55 mu m. The e r and Qxf exhibited trends resemble that of apparent densities. The variation of Ty mainly originated from the large and negative If of LBSCA glass. Particularly, the LZS-1.2 wt% LBSCA ceramic obtained at 925 degrees C displayed a compact and uniform microstructure and possessed optimum microwave dielectric characteristics of epsilon(r) = 10.51, Qxf= 31700 GHz, tau(f) = -7.93 ppm/degrees C. Moreover, LZS-1.2 wt% LBSCA ceramic exhibited favorable compatibility with silver, endowing the material with possible application in low temperature co-fired ceramic (LTCC).