Abstract:Low-temperature-fired Li2Zn1−xCoxTi3O8 (x = 0, 0.03, 0.04, 0.05, 0.06, 0.07) ceramics with 1.5 wt% Li2O–B2O3–SiO2–CaO–Al2O3 (LBSCA) glass as sintering aid were attained through a traditional solid-state-reaction method, and the relationship between their structures and microwave dielectric properties were thoroughly investigated. X-ray diffraction patterns revealed that the solid solutions composed of Li2ZnTi3O8 and Li2CoTi3O8 were produced. The main peaks were identified with the cubic spinel phase of the Li2(Zn,Co)Ti3O8. Co substitution successfully lowered the sintering temperature of Li2ZnTi3O8 to approximately 900 °C and accelerated its densification when LBSCA glass was used as the sintering aid. The cobalt content considerably influenced grain homogeneity, grain size and dielectric polarizability, as well as the variation in relative permittivity (εr) and quality factor (Q × f). When x = 0.04, Li2Zn0.96Co0.04Ti3O8 ceramic sintered at 900 °C had the most uniform grain size and exhibited optimum microwave dielectric properties, having a relative permittivity of 21.61, Q × f of 79,100 GHz and temperature coefficient of resonance frequency (τf) of − 12.3 ppm/°C. Thus, it showed potential for low temperature co-fired ceramic applications.

Microwave Dielectric Properties and Low Temperature Sintering of Li 2 Zn(Ti 1−x Sn X ) 3 O 8 (x ≤ 0.20) Ceramics with B 2 O 3 –cuo Addition

Microwave Dielectric Properties and Low Temperature Firing of (1 − X)li2zn3ti4o12 –xli2tio3 (0.2 ≤ X ≤ 0.8) Ceramics with B2O3–CuO Addition

Microwave Dielectric Properties and Low-Temperature Sintering of (zn0.8mg0.2)2sio4–tio2 Ceramics with Li2O–B2O3

Structure and Microwave Dielectric Behaviour of Low-Temperature-fired Li2Zn1−xCoxTi3O8 (x = 0–0.07) Ceramics for Low Temperature Co-Fired Ceramic Applications

Microwave dielectric properties and low temperature firing of (1 − )LiZnTiO LiTiO (0.2 ≤ ≤ 0.8) ceramics with BO–CuO addition

Microwave dielectric properties of low-firing Li2MO3 (M=Ti, Zr, Sn) ceramics with B2O3-CuO addition

A new low-loss microwave dielectric ceramic for low temperature cofired ceramic applications

Microwave Dielectric Properties of the Low-Temperature-fired Li2ZnTi3O8–Li2TiO3 Ceramics for LTCC Applications

The effect of composition on Li2(Mg0.3Zn 0.7)Ti3O8-xTiO2 microwave dielectric ceramics for low temperature co-fired ceramics technology application

Microwave dielectric properties of low-fired Li2SnO3 ceramics co-doped with MgO–LiF

Microwave Dielectric Properties and Low Temperature Sintering Behavior of Li2coti3o8 Ceramic

Microwave Dielectric Properties and Compatibility with Silver of Low-Fired Li2cu0.1zn0.9ti3o8 Ceramic

Effect of ZnO and B2O3 on the Sintering Temperature and Microwave Dielectric Properties of LiNb0.6Ti0.5O3 Ceramics

Preparation and Characterization of (Co0.3zn0.7)(ti1-Xsnx)nb2o8 Microwave Dielectric Ceramics

Microwave Properties of Low-Fired Li2ZnTi3O8 Ceramics Doped with CuO–Bi2O3–V2O5

Low Temperature Sintering of Li 2 (mg 0.3 Zn 0.7 )ti 3 O 8 -0.12Tio 2 Microwave Dielectric Ceramics with Controllable Grain Size

Preparation and characterization of (Co<sub>0:3</sub>Zn<sub>0:7</sub>)(Ti<sub>1–x</sub>Sn<sub>x</sub>)Nb<sub>2</sub>O<sub>8</sub> microwave dielectric ceramics

Microwave dielectric properties of temperature stable Li2ZnxCo1−xTi3O8 ceramics

Low Temperature Cofiring and Compatibility with Silver Electrode of ZnO–SnO2–TiO2–Nb2O5 Ceramics with BaCu(B2O5) Addition

Structure and microwave dielectric properties of (Zn 0.3 Co 0.7 )Ti 1−x Sn x O 3 ceramics

Low-temperature Sintered Li2(MnxTi1−x)O3 Microwave Dielectric Ceramics with Adjustable Τf