Evaluation of Zn‐substituted La0.5Sr0.5CoO3 Ceramics As Functional Materials for Thick‐film Resistors
Yongcheng Lu,Rui Peng,Yuanxun Li,Fuyu Li,Yuanjing Zhang,Daming Chen,Qiye Wen,Qinghui Yang
DOI: https://doi.org/10.1111/jace.18290
IF: 4.186
2022-01-01
Journal of the American Ceramic Society
Abstract:This work focuses on the evaluation of La0.5Sr0.5Co1-xZnxO3 (LSCZ, x = 0.00-0.10) ceramics as an air-fireable and economical functional material for thick film resistors. Solid-state reaction experiments and first-principles calculations were conducted to investigate the crystal structure, thermal behaviors, and electrical properties of LSCZ ceramics. The substitution of Zn2+ modified the bond properties, electron distribution, and band structure, resulting in more serious structural deformation, increasing the bond population of Co-O and weakening the charge transfer of LSCZ. Experimental results showed that the addition of Zn2+ lowered the densification temperature, activation energy, and crystallite size. As the ratio of Zn2+ increased, the conductivity and temperature coefficient of resistance showed a downward trend. Impedance variation with frequency and thermal aging tests were also performed. For the x = 0.05 specimen sintered at 1200 degrees C, values of 95.5% for relative density, 2857 S/cm for conductivity, 1267 ppm/degrees C for temperature coefficient of resistance, -0.47% for conductivity change could be achieved.