Preparation and characterization of LaMn 0.5 Co 0.5 O 3 –Ni 0.66 Mn 2.34 O 4 composite NTC ceramics

Cuiping Huang,Long Chen,Qinan Zhang,Shannan Chang,Bo Zhang,Aimin Chang,Huimin Zhang

DOI: https://doi.org/10.1007/s10854-016-4737-5

2016-01-01

Abstract:Negative temperature coefficient (NTC) thermistor materials based on (LaMn 0.5 Co 0.5 O 3 ) x –(Ni 0.66 Mn 2.34 O 4 ) 1−x (0 ≤ x ≤ 0.5) composite ceramics, are fabricated by the conventional solid-state reaction method. The crystal structure, surface morphology and electrical properties of the composite ceramics are investigated and characterized by X-ray powders diffraction (XRD), scanning electron microscope (SEM), and Agilent digital multimeter, respectively. XRD results show that main phases of as-sintered ceramics are a cubic spinel structure Ni 0.66 Mn 2.34 O 4 phase and a rhombohedral perovskite structure LaMn 0.5 Co 0.5 O 3 phase. SEM images indicate that the grain size of the composite ceramics decreases with increasing the low-resistivity perovskite phase. The ρ 25 and B value of the composite ceramics decreases with increasing x, and the B is still reasonably high in the range of 4000–3500 K when x ≤ 0.2. Meanwhile, the introduction of the perovskite phase leads to a decrease in the resistance drift, which the ΔR/R 0 is relatively low (0.26–1.8 %) after annealing at 125 °C for 600 h in air atmosphere. These findings exhibit that (LaMn 0.5 Co 0.5 O 3 ) x –(Ni 0.66 Mn 2.34 O 4 ) 1−x (0 ≤ x ≤ 0.5) composite ceramics have a higher electrical stability in comparison with Ni 0.66 Mn 2.34 O 4 ceramics, are helpful for meeting demands for obtaining better stability and performance of NTC composites ceramics.