Crystal structure, cation distribution and electrical properties in Ni Al Mn3−−O4 (0 < x < 0.6; 0 < y < 0.3) spinel-based NTC chip thermistors

Gang-Qin Shao,Quan-Jin Cen,Zhi-Hua Chen,Ji-Wei Zhang,Meng-Xiang Xie,Qiang Li,Xiu-Hua Cao,Wen-Hao Wang,Yan-Pei Wang,Hou-Ran Wu,Chun-Yuan Hu

DOI: https://doi.org/10.1016/j.ceramint.2024.03.222

IF: 5.532

2024-03-01

Ceramics International

Abstract:Ni x Al y Mn3−x−y O4 (0 &lt; x &lt; 0.6; 0 &lt; y &lt; 0.3) series NTC chip thermistors with homogeneous chemical compositions and high-pure spinel phases were fabricated via a tape casting-lamination-sintering process. The multi-variate cation distribution model was established as ( Mn 1 x + v 2 + Ni x v 2 + ) [ Mn 22 v y 3 + Mn v 4 + Ni v 2 + Al y 3 + ] O 4 (0 &lt; v &lt; 0.5). The conduction mechanism was proposed based on a nearest neighbor hopping (NNH) model. They were verified coherently by cation-oxyanion chemical compositions (XRF/EDS), valence states (XPS), phase structures and Rietveld refinements (XRD), IR vibrations and electrical analyses. The obtained NTC chips were well suitable for commercial applications with a high reliability and with regulable ρ25 (4080 ± 135–15,760 ± 526 Ω cm) and B25/50 (4016 ± 20–4251 ± 13 K).

materials science, ceramics