Enhanced temperature range and stability in LaAlO 3 NTC ceramics through Ce-Nb codoping
Yan Xue,Wenye Deng,Jinyang Li,Yi Liu,Ni Ai,Pengjun Zhao,Aimin Chang,Huimin Zhang,Yongxin Xie
DOI: https://doi.org/10.1016/j.jallcom.2024.177557
IF: 6.2
2024-11-24
Journal of Alloys and Compounds
Abstract:Negative temperature coefficient (NTC) thermistors have garnered increased attention due to their high sensitivity, low thermal inertia, and cost-effectiveness. However, their practical application is significantly constrained by a limited temperature range and poor stability. In this study, a series of Ce-Nb codoped LaAlO 3 ceramics were synthesized using the traditional solid-state reaction method, and their unique electrical properties as NTC thermistors were examined. XRD analysis reveals that Ce-Nb codoping induces lattice distortion in the LaAlO 3 ceramics. HAADF-STEM shows that Ce replaces La at A-sites, while Nb substitutes for Al at B-sites. XPS indicates that the substitution of Ce 4+ for La 3+ and Nb 5+ for Al 3+ facilitates the formation of oxygen vacancies and enhances the number of free carriers. Electrical resistance and UV measurements demonstrate that increasing the Ce and Nb doping levels improves carrier mobility and reduces the band gap of LaAlO 3 . These modifications significantly enhance the electrical performance and extend the temperature range to 298 K –1773 K when the Ce doping level is 0.2 and the Nb doping level is 0.1. Additionally, aging tests indicate that Ce-Nb co-doping reduces the aging drift of LaAlO 3 to 0.38 % after 500 h of aging at 1273 K. This novel Ce-Nb codoped LaAlO 3 ceramic, with its broad temperature range and superior stability, shows significant potential for application in NTC thermistors.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering