Effect of Ni Substitution on Electrical and Thermoelectric Properties of LaCoO3 Ceramics

Fu Li,Jing-Feng Li

DOI: https://doi.org/10.1016/j.ceramint.2010.08.024

IF: 5.532

2010-01-01

Ceramics International

Abstract:LaCo1−xNixO3 (0≤x≤0.2) ceramics were prepared by solid state reaction and their thermoelectric properties were investigated from room temperature (RT) to 400°C. In the range from RT to 180°C, LaCoO3 showed a large negative Seebeck coefficient, but it changed to a positive value above 180°C. However, the Seebeck coefficient became positive in the whole investigated temperature span due to Ni substitution for Co even for a tiny amount, but its absolute value decreased significantly with increasing Ni content. The LaCo0.9Ni0.1O3 composition showed an enhanced power factor with a maximum value of 1.41×10−4Wm−1K−2 at room temperature, which is about 3.5 times higher than that of un-doped LaCoO3. Because the power factor decreased and the thermal conductivity increased apparently with temperature, the ZT values were not increased at elevated temperatures, in spite of a relatively large ZT value of 0.031 at a low temperature (50°C) obtained in the composition LaCo0.9Ni0.1O3.