High–performance Copper–substituted La0.5Sr0.5CoO3 Ceramics As Economical Functional Materials for Thick Film Resistors

Yongcheng Lu,Yuanxun Li,Fuyu Li,Daming Chen,Qinghui Yang,Xiangming Zeng

DOI: https://doi.org/10.1016/j.ceramint.2024.05.290

IF: 5.532

2024-01-01

Ceramics International

Abstract:The demand for cost–effective materials for thick film resistors has driven the exploration of alternative functional materials to replace the traditionally used ruthenium oxides. This study investigates the synthesis and properties of copper–substituted La0.5Sr0.5CoO3 (La0.5Sr0.5Co1-xCuxO3, LSCCu, x = 0.02–0.10) ceramics as a potential economical substitute. The crystal structure, electrical performance, and sintering behavior of LSCCu with varying Cu2+ contents were characterized through solid–state reactions and first–principles simulations. The results indicate that the perovskite structure is maintained with increasing Cu2+, while the densification temperature, crystallinity, and conductivity decrease. Moreover, Cu2+ substitution reduced the DOS across the Fermi level and weakened the electron transport in LSCCu. The sample with x = 0.06 exhibited a promising conductivity of 2609 S/cm after sintering at 1150 °C, comparable to commercial thick film resistor materials. The temperature coefficient of resistance (TCR) of LSCCu showed a metallic behavior with a low value of 1148 ppm/°C for the x = 0.06 sample. Additionally, the LSCCu ceramics possess good long–term stability and frequency stability of resistance. These findings suggest that LSCCu ceramics are a promising economical material for thick film resistor applications.