Abstract:Cu matrix composites have received increased attention in a wide industrial area because of their excellent mechanical properties and good electrical and thermal conductivity. However, the addition of general ceramic reinforcements often leads to a marked reduction in electrical conductivity for Cu matrix composites. In this study, the ZrB 2 -reinforced Cu composites have been developed to overcome this drawback since these metal borides possess relatively high electrical conductivity. The 5 wt.% ZrB 2 /Cu composites were prepared using hot-pressed sintering techniques at varying temperatures from 760 to 920°C. The influence of sintering temperature on the microstructure, relative density, and mechanical and electrical properties was examined. The results of the SEM observation show that ZrB 2 particles are seamlessly integrated into the Cu matrix for all ZrB 2 /Cu composites. The average grain size of the Cu matrix increases from 360 to 980 nm with the increase of the sintering temperature. The increase in sintering temperature also leads to the surface porosity decrease from 1.4 to 0.4%. The relative density and electric conductivity of the composites increase at the same time as the sintering temperature increases. However, microhardness increases and decreases, with a maximum value of 92 HV0.2 achieved at 840°C. The elastic modulus and nanohardness maps determined from the nanoindentation indicate that the reinforced ZrB 2 particles demonstrate the highest values for elastic modulus (340–500 GPa) and nanohardness (30–48 GPa). At the same time, the Cu matrix possesses a modulus of 100–200 GPa and nanohardness of about 10 GPa. TEM observation confirmed that the sintering temperature exhibits little influence on the interface reaction between ZrB 2 and Cu. Both sharp interface and interface with amorphous transition layer are observed. The variation of microhardness is mainly due to the strengthening of grain refinement and to the mismatch of the thermal expansion coefficients. The above results can provide further insights into the deeper understanding of the role of sintering temperature during hot-pressed sintering.

Effect of the Cooling Ways on the Properties and Microstructure of ZrO2/ZrW2O8 Ceramic Composites

Microstructure and properties of SrTiO3/ZrO2 ceramic composites prepared through pressureless sintering

Effect of sintering temperature and holding time on the microstructure and mechanical properties of ZrB2–SiCw composites

Effect of Sintering Temperature on the Microstructure and Properties of High-Strength and Highly Conductive 5 wt.% ZrB2/Cu Composite

Effects of ZrB2 on Mechanical Properties of Al2O3-ZrB2-SiC Composite Ceramics at Room Temperature

Effect of Zr2Al4C5 Content on the Mechanical Properties and Oxidation Behavior of ZrB2-SiC-Zr2Al4C5 Ceramics

Effect of Quenching-Free Method on the Microstructure and Properties of Low-Temperature Sintered Glass-Ceramic Composites

Reaction mechanisms and properties of in situ porous Al2O3-ZrO2-mullite composites

Study on Mechanical Properties of Hot Pressing Sintered Mullite-Zro2 Composites with Finite Element Method

Effects of Composite Systems on Sintering Properties of Aluminum Oxide Ceramics

Preparation and properties of a porous ZrO 2 /SiZrBOC ceramic matrix composite with high temperature resistance and low thermal conductivity

Effect of Sintering Temperature on Compressive Strength of Porous Yttria-Stabilized Zirconia Ceramics

Preparation of Porous Spodumene/zircon Composite Ceramics and Its Thermal and Mechanical Properties

Effect of alloying element Zr on microstructure and properties of Cu−Y2O3 composites

Microstructure and Mechanical Properties of Hot-Pressed Al2O3–mullite–ZrO2–SiC Composites

Microstructure and Mechanical Properties of ZTA Composites Fabricated by Oscillatory Pressure Sintering

Characterization of hot-pressed short carbon fiber reinforced ZrB2–SiC ultra-high temperature ceramic composites

Synergistic strengthening and toughening of oscillatory pressure sintered WC-ZrO2-Al2O3 ceramics

Effect of MgO addition on properties of reaction-sintered ZrO2-toughened Al2O3 multiphase ceramic

Size Effect on the Thermal Expansion of ZrO2/ZrW2O8 Composites Fabricated by the Conventional Sintering Process

Influence of Y2O3 contents on sintering and mechanical properties of B4C-Al2O3 multiphase ceramic composites