Thermal decomposition and crystallization behavior of Yb/Y co-doped SrZrO3 precursor used in the suspension plasma spray process
Yuanming Gao,Yu Bai,Peng Zhang,Weicheng Liang,Qi Liu,Shufang Yan,Jiao Huang,Hongying Dong,Ruigang Wang,Wen Ma
DOI: https://doi.org/10.1016/j.surfcoat.2021.127991
IF: 4.865
2022-01-01
Surface and Coatings Technology
Abstract:A double rare-earth (Yb/Y) co-doped SrZrO3 [Sr1.0(Zr0.9Yb0.05Y0.05)O2.95] thermal barrier coating was prepared via suspension plasma spraying (SPS). The rare-earth nitrates [Zr(NO3)4·5H2O, Sr(NO3)2, Yb(NO3)3·6H2O, Y(NO3)3·6H2O] and NH4(C2O4)2·H2O were used to prepare the precursor suspension by co-precipitation. The thermal decomposition and crystallization of the precursor suspension powders calcined at 1200 °C were characterized with X-ray diffraction and a synchronous thermal analyzer coupled with quadrupole mass spectrometry. Zr2(C2O4)2(OH)4 decomposed into Zr(C2O4)2, ZrO2, and H2O initially, followed by the decomposition of Zr(CO3)2 into ZrO2. The SrC2O4 precursor decomposed into SrCO3and SrO consecutively. The ZrO2 reacted with SrO (Yb2O3, Y2O3) to generate the Yb/Y co-doped SrZrO3 . And the Yb/Y co-doped SrZrO3 coating with a columnar crystal structure was prepared by SPS, which was analyzed with scanning electron microscopy, an inductively coupled plasma atomic emission spectrometer, and a laser flash analyzer. The thermal conductivity of the as-prepared coating was 1.77 W·m−1·K−1 at 1000 °C, which was more than 19% lower than that of the SPS SrZrO3 coating.
physics, applied,materials science, coatings & films