Abstract:A series of ( Fe 0.86 Zr 0.033 Nb 0.033 B 0.068 Cu 0.01)x( Al 2 O 3)1-x granular films of about 100 nm thick were deposited on the glass substrate using the magnetron sputtering technique. Hall resistivity was measured using a four-terminal method at room temperature in the field of 1.1 Tesla. As x increases, the Hall resistivity of the samples rises and reaches a maximum of 17.5 μΩ-cm at x = 0.43, which is about three orders of magnitude greater than those of pure magnetic metal samples, and for further increase of x, the Hall resistivity decreases. For as-deposited x = 0.43 sample, transmission electron microscopy (TEM) images shows the microstructural characteristics of granular films around percolation threshold. The temperature dependence of resistivity shows that the conduction behavior changes from insulator to metal with the increment of metal fraction, and for sample x = 0.43, the conduction behavior is located in the transition region from insulator to metal, near the percolation value, which is consistent with the above experimental results. It is suggested that the enhancement of Hall effect results from not only the magnetic metal fraction but also the microstructure characteristic of percolation system.

Hall Effect of (co 0.34 Fe 0.66 ) 0.42 (sio 2 ) 0.58 Granular Films

Hall Effect Of (Co0.34fe0.66)(0.42)(Sio2)(0.58) Granular Films

The Hall Effect of Co0.35fe0.65-Al2o3 Nanogranular Films

Investigation on the Giant Hall Effect of (fexsn100−x)1−y(sio2)y Granular Films

THE HALL EFFECT AND MICROSTRUCTURES OF (Fe0.86zr0.033nb0.033b0.068cu0.01)x(al2o3)1-Xgranular FILMS

THE HALL EFFECT AND MICROSTRUCTURES OF (<font>Fe</font><sub>0.86</sub><font>Zr</font><sub>0.033</sub><font>Nb</font><sub>0.033</sub><font>B</font><sub>0.068</sub><font>Cu</font><sub>0.01</sub>)<sub>x</sub>(<font>Al</font><sub>2</sub><font>O</font><sub>3</sub>)<sub>1-x</sub> GRANULAR FILMS

Giant Hall Effect of Fe 45.51 (al 2 O 3 ) 54.49 Nano-granular Film

Giant Hall Effect Of Fe-45.51(Al2o3)(54.49) Nano-Granular Film

Giant Hall Effect In Fexsn100-X Granular Alloy Films

Co-based Nanogranular Thin Films on Flexible Substrate for Gigahertz Applications

Soft Magnetism and Microwave Magnetic Properties of Fe-Co-Hf Films Deposited by Composition Gradient Sputtering

The Hall Effect of Fe–Al–O Thin Film

Dissipationless Anomalous Hall Current in $Fe_{100-x}(SiO_2)_x$ Films

High-frequency Electromagnetic Properties of Compositionally Graded FeCoB-SiO2 Granular Films Deposited on Flexible Substrates

Giant Magnetoresistance of Co-Sio2 Nano-Granular Films

Magnetic Properties of FeSi-SiO2 Granular Films

Soft Magnetic Properties Of Sequential Deposited Co40fe40b20/Sio2 Multilayer Nanogranular Films For High Frequency Applications

Soft Magnetic Properties and Microwave Permeability of Multilayer Nanogranular Films with High Resistivity

Percolation and Microwave Characteristics of CoFeB–SiO2 Nano-Granular Films

Giant Hall effect in two-dimensional CoSi$_2$ granular arrays

Effect of SiO2 on the electromagnetic characteristics of lossy CoFeB-SiO2 nanogranular films