Dissipationless Anomalous Hall Current in $Fe_{100-x}(SiO_2)_x$ Films

W. J. Xu,B. Zhang,Z. Wang,W. Li,R. H. Yu,X. X. Zhang

DOI: https://doi.org/10.1103/PhysRevB.83.205311

2010-04-13

Abstract:The observation of dissipationless anomalous Hall current is one of the experimental evidences to confirm the intrinsic origin of anomalous Hall effect. To study the origin of anomalous Hall effect in iron, Fe$_{100-x}$(SiO$_{2}$)$_{x}$ granular films with volume fraction of SiO$_{2}$ 0\le x \le 40.51 were fabricated using co-sputtering. Hall and longitudinal resistivities were measured in the temperature range 5 to 350 K with magnetic fields up to 5 Tesla. As x increased from 0 to 40.51, the anomalous Hall resistivity and longitudinal resistivity increased about 4 and 3 orders in magnitude, respectively. Analysis of the results revealed that the normalized anomalous Hall conductivity is a constant for all the samples, the evidence of dissipationless anomalous Hall current in Fe.

Mesoscale and Nanoscale Physics,Other Condensed Matter

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to verify the intrinsic mechanism of the Anomalous Hall Effect (AHE) in iron (Fe), and confirm this mechanism by experimentally observing the dissipationless anomalous Hall current. Specifically, the author hopes to reveal the essence of AHE by studying the changes in Hall resistivity and longitudinal resistivity in Fe₁₀₀₋ₓ(SiO₂)ₓ films with different SiO₂ volume fractions (0 ≤ x ≤ 40.51).

### Background and Problem Description of the Paper

The Anomalous Hall Effect (AHE) is a phenomenon observed in ferromagnetic materials. Its physical mechanisms can be divided into extrinsic mechanisms (such as side - jump and skew scattering) and intrinsic mechanisms. The intrinsic mechanism originates from the Berry - phase effect of the electron wave function, while the extrinsic mechanism is related to impurity scattering. Theoretically, if AHE is intrinsic, the normalized anomalous Hall conductivity should be a constant and not change with the change of impurities or electron relaxation time. This can be verified by observing the square - dependence of the anomalous Hall conductivity on the carrier density, that is:

\[
\sigma_{xy} \propto \rho_{xx}^2 / n
\]

where \(\sigma_{xy}\) is the anomalous Hall conductivity, \(\rho_{xx}\) is the longitudinal resistivity, and \(n\) is the carrier density.

### Experimental Design and Results

To verify this, the author prepared Fe₁₀₀₋ₓ(SiO₂)ₓ films with different SiO₂ volume fractions and measured the Hall resistivity and longitudinal resistivity of these samples in the temperature range from 5 K to 350 K. With the increase of SiO₂ content, the longitudinal resistivity and the anomalous Hall resistivity increased by about 3 and 4 orders of magnitude respectively. By analyzing the data, the author found that the normalized anomalous Hall conductivity remained constant, indicating that the dissipationless anomalous Hall current was observed in iron.

### Conclusion

This research is the first to observe the dissipationless anomalous Hall current in a simple ferromagnetic metal, which provides direct evidence for the intrinsic mechanism of AHE. In addition, the research also emphasizes that when performing reliable scaling - law fitting, there needs to be a sufficient range of changes in longitudinal resistivity and AHE resistivity.

### Formula Summary

- Relationship between anomalous Hall resistivity and longitudinal resistivity:
\[
\rho_{xy} = R_0 H+\frac{S}{4\pi} M
\]
where \(\rho_{xy}\) is the Hall resistivity, \(R_0\) is the ordinary Hall coefficient, \(H\) is the magnetic field, \(S\) is a constant, and \(M\) is the magnetization intensity.

- Square - dependence of normalized anomalous Hall conductivity:
\[
\sigma_{xy} \propto \frac{\rho_{xx}^2}{n}
\]

- Scaling law:
\[
\rho_{xy} \propto \rho_{xx}^\gamma
\]

Through the analysis of these formulas and experimental data, the author successfully proved the intrinsic nature of AHE in iron.