Solvent-Mediated Synthesis of Amorphous Li 3 PS 4 /Polyethylene Oxide Composite Solid Electrolytes with High Li + Conductivity

Ethan C. Self,Zachary D. Hood,Teerth Brahmbhatt,Frank M. Delnick,Harry M. Meyer,Guang Yang,Jennifer L. M. Rupp,Jagjit Nanda

DOI: https://doi.org/10.1021/acs.chemmater.0c01990

IF: 10.508

2020-09-21

Chemistry of Materials

Abstract:Solvent-mediated routes have emerged as an effective, scalable, and low-temperature method to fabricate sulfide-based solid-state electrolytes. However, tuning the synthesis conditions to optimize the electrolyte's morphology, structure, and electrochemical properties is still underexplored. Here, we report a new class of composite solid electrolytes (SEs) containing amorphous Li₃PS₄ synthesized in situ with a poly(ethylene oxide) (PEO) binder using a one-pot, solvent-mediated route. The solvent and thermal processing conditions have a dramatic impact on the Li₃PS₄ structure. Conducting the synthesis in tetrahydrofuran resulted in crystalline β-Li₃PS₄ whereas acetonitrile led to amorphous Li₃PS₄. Annealing at 140 °C increased the Li⁺ conductivity of an amorphous composite (Li₃PS₄ + 1 wt % PEO) by 3 orders of magnitude (e.g.<i>,</i> from 4.5 × 10^–9 to 8.4 × 10^–6 S/cm at room temperature) because of: (i) removal of coordinated solvent and (ii) rearrangement of the polyanionic network to form P₂S₇^4– and PS₄^3– moieties. The PEO content in these composites should be limited to 1–5 wt % to ensure reasonable Li⁺ conductivity (e.g.<i>,</i> up to 1.1 × 10^–4 S/cm at 80 °C) while providing enough binder to facilitate scalable processing. The results of this study highlight a new strategy to suppress crystallization in sulfide-based SEs,, which has important implications for solid-state batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.chemmater.0c01990?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.chemmater.0c01990</a>.XRD patterns; Raman spectra; SEM/EDX images; slurry casting studies (<a class="ext-link" href="/doi/suppl/10.1021/acs.chemmater.0c01990/suppl_file/cm0c01990_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,chemistry, physical

What problem does this paper attempt to address?

The problems that this paper attempts to solve mainly focus on developing a new type of composite solid electrolyte material to improve the performance of lithium - ion batteries. Specifically, researchers synthesized a composite solid electrolyte containing amorphous Li₃PS₄ and polyethylene oxide (PEO) binder through a solvent - mediated method, aiming at:

1. **Optimizing the morphology, structure and electrochemical properties of the electrolyte**: By adjusting the synthesis conditions (such as solvent selection, heat treatment conditions and binder content), explore how to optimize the performance of these composite solid electrolytes, especially their lithium - ion conductivity.

2. **Inhibiting the crystallization of sulfide - based solid electrolytes**: It has been found that the crystallinity of Li₃PS₄ can be controlled by synthesis in a specific solvent. For example, using tetrahydrofuran (THF) as a solvent will lead to the formation of crystalline β - Li₃PS₄, while using acetonitrile (AN) will produce amorphous Li₃PS₄. Amorphous materials may contribute to promoting the uniform deposition / stripping of lithium ions due to the lack of obvious grain boundaries, thereby improving the long - term cycling stability of the full cell.

3. **Increasing the lithium - ion conductivity**: By heat treatment (such as annealing at 140 °C) to remove the coordinating solvent and rearrange the polyanion network, the lithium - ion conductivity of the amorphous composite can be significantly increased. For example, for an amorphous composite containing 1 wt% PEO, the lithium - ion conductivity increases from 4.5×10⁻⁹ S/cm at room temperature to 8.4×10⁻⁶ S/cm.

4. **Balancing conductivity and processability**: The study also explored the influence of PEO content on the lithium - ion conductivity of the composite, and found that the PEO content should be limited to 1 - 5 wt% to ensure a reasonable lithium - ion conductivity while providing sufficient binder to promote large - scale processing.

In summary, this paper developed a new amorphous Li₃PS₄/PEO composite solid electrolyte through a solvent - mediated synthesis method, aiming to solve the limitations of traditional sulfide - based solid electrolytes in lithium - ion battery applications, especially to improve their lithium - ion conductivity and processability, and to inhibit uneven lithium growth.