Abstract:The novel bismuth-substituted rare earth iron garnet films were grown by the modified liquid phase epitaxy (LPE) technique for use as a 45degrees faraday rotator in optical isolators. First, single crystals of Y3Fe5O12(YIG), with a lattice, constant of 1.2378 nm, were grown by means of the Czochralski method. Using YIG instead of the conventional nonmagnetic garnet of Gd3Ga5O12(GGG) as a substrate, a film of BiYbIG was grown by means of the LPE method from Bi2O3-B2O3 fluxes. The structural, magnetic and magneto-optical properties of BiYbIG LPE film/YIG crystal composite were investigated using X-ray diffraction (XRD), electron probe microanalysis (EPMA), vibrating sample magnetometry (VMS) and near-infrared transmission spectrometry. The saturation magnetization 47piM(s) was estimated to be about 1200 G. The Faraday rotation spectrum was measured by the method of rotating analyzer ellipsometry (RAE) with the wavelength varied from 800 to 1700 nm. The resultant Bi0.37Yb2.63Fe5O12 LPE film/YIG crystal composite shows an increased Faraday rotation coefficient due to doping W, ions on the dodecahedral sites of the magnetic garnet without increasing absorption loss, therefore a good magneto-optic figure of merit, defined by the ratio of Faraday rotation and optical absorption loss, can achieved of 21.5 and 30.2degrees/dB at 1300 and 1550 nm wavelengths respectively at room temperature. Since Yb3+ ions and Y3+ ions provide the opposite contributes to the wideband and temperature characteristics of Faraday rotation, the values of Faraday rotation wavelength and temperature coefficients are reduced to 0.06%/nm and 0.007 degrees(.) degreesC(-1) at 1550 nm wavelength respectively.

Terahertz Response of Bi-substituted Rare-Earth Iron Garnet

Terahertz Magneto-Optical Response of Bismuth-Gadolinium-substituted Rare-Earth Garnet Film

Mixed rare-earth iron garnet AYbBiIG single-crystals for high-performance optical isolation

A mixed rare-earth iron garnet single crystal of ReYbBiIG for high-performance magneto-optical devices

Enhanced Terahertz Magneto-Optical Performance in Substrate-Free Ultra-Thick TbErBi:RIG Crystal Films

Faraday Rotation Spectra Analysis Of Bi-Substituted Mixed Rare-Earth Iron Garnet Crystals In Optical Communication Band

Bismuth-substituted yttrium iron garnet film/frystal composite for Faraday rotators

Faraday rotation spectra of bismuth-substituted ferrite garnet films with in-plane magnetization

Research of preparing Bi substituted yttrium iron garnet and epoxy magneto-optical hybridized films

The Absorption Property of Single Crystal Lubiig Garnet Film in Terahertz Band

An Artificially Garnet Crystal Materials Using in Terahertz Waveguide

High Figure of Merit Magneto‐Optical Ce‐ and Bi‐Substituted Terbium Iron Garnet Films Integrated on Si

Terahertz magneto-optical effect of wafer-scale La: yttrium iron garnet single-crystal film with low loss and high permittivity

Growth and Characterization of Magneto-Optical Single-Crystal Reybbiig with Temperature-Stabilized Faraday Rotation

The thickness effect on the compensation temperature of rare-earth garnet thin films

Faraday rotation and sensitivity of (100) bismuth-substituted ferrite garnet films

Faraday-Rotation in Iron Garnet Films Beyond Elemental Substitutions

Nanometer thick magneto-optical iron garnet films

Dynamic Performance of Magneto-Optical Bi-substituted Rare-Earth Iron Garnet

Liquid-Phase Epitaxial Growth of 3 in Diameter Bismuth-Doped Thulium Iron Garnet Films for Magneto-Optical Applications

Terahertz Faraday Rotation Of Magneto-Optical Films Enhanced By Helical Metasurface