Abstract:Y3Fe5O12 (YIG) crystals are highly desirable for the fabrication of mid-infrared isolators with the rapid growth of optical communications, although it is rather challenging to grow large size and high-quality single crystals. Dy3+ doping is expected to improve the optical and magneto-optical properties. However, high quality Dy:YIG crystals and the adjustment of Dy3+ on the structure and optical behavior of YIG crystal remain unclear, impeding its practical applications. Herein, a series of Y3– xDyxFe5O12 (x = 0, 0.5, 1.0, 1.5, 3) solid solution crystals was grown by the flux-Bridgman method and single crystals up to 25 mm were obtained. With the introduction of Dy3+, lattice parameters are gradually enlarged from 1.2379 nm (YIG) to 1.2420 nm (DyIG). Typical Dy3+ absorption peaks are observed around 1070, 1265 and 1670 nm. The refractive index decreases from 2.37 (500 nm) to 2.10 (2500 nm) for YIG crystal, and it reduces from 2.47 (500 nm) to 2.16 (2500 nm) for DyIG crystal. The optical bandgaps remain almost unchanged for Dy:YIG crystals. The optical dispersion of the refractive indices was finely fitted by the Wemple and DiDomenico (WDD) and the Sellmeier models, respectively. With the increase of Dy3+ content, the saturation magnetization (M s ) decreases significantly from 23.62 emu/g (YIG) to 5.33 emu/g (DyIG). Small coercive field is persisted for this system, endowing small external magnetic field. These results provide valuable references for the manipulation of rare earths on the properties of magneto-optical crystals, which is beneficial to the design of high-performance garnet crystals for the application of optical switching and non-reciprocal related devices.

Terahertz magneto-optical effect of wafer-scale La: yttrium iron garnet single-crystal film with low loss and high permittivity

Mixed rare-earth iron garnet AYbBiIG single-crystals for high-performance optical isolation

Terahertz Wave Responses of Dispersive Few-Layer Graphene (flg) and Ferroelectric Film Composite

Bismuth-substituted yttrium iron garnet film/frystal composite for Faraday rotators

Nanometer-Thick Yttrium Iron Garnet Films with Perpendicular Anisotropy and Low Damping

A mixed rare-earth iron garnet single crystal of ReYbBiIG for high-performance magneto-optical devices

Growth and Characterization of Magneto-Optical Single-Crystal Reybbiig with Temperature-Stabilized Faraday Rotation

Supplemental Materials for “ Photo-Spin-Voltaic Effect ”

Yttrium Iron Garnet Thin Films with Very Low Damping Obtained by Recrystallization of Amorphous Material

Giant reduced magnetic anisotropy in magneto-optical garnet

Pulsed laser deposition of epitaxial yttrium iron garnet films with low Gilbert damping and bulk-like magnetization

Origin of high-frequency magnetic loss of Y3Fe5O12 single crystal thin films prepared with high-throughput screening by magnetron sputtering

Fabrication and characterizations of a Gadolinium doped terbium gallium garnet crystal for Faraday rotators

Effective Faraday Rotator Based on the TbYO3 Crystal with a High Verdet Constant and a High Thermal Conductivity.

Growth and characterization of holmium-doped yttrium iron garnet single crystal

Ferromagnetic resonances in single-crystal yttrium iron garnet nanofilms fabricated by metal-organic decomposition

Ferromagnetic Resonance Studies of Strain tuned Bi:YIG Films

Wafer-level substrate-free YIG single crystal film for a broadband tunable terahertz isolator

Growth, optical dispersion and magnetic behavior of Dy3+ doped yttrium iron garnet crystals

Fabrication and broadband ferromagnetic resonance studies of freestanding polycrystalline yttrium iron garnet thin films

Perpendicularly magnetized YIG films with small Gilbert damping constant and anomalous spin transport properties