Abstract:Y3Fe5O12 (YIG) crystals are highly desirable for the fabrication of mid-infrared isolators with the rapid growth of optical communications, although it is rather challenging to grow large size and high-quality single crystals. Dy3+ doping is expected to improve the optical and magneto-optical properties. However, high quality Dy:YIG crystals and the adjustment of Dy3+ on the structure and optical behavior of YIG crystal remain unclear, impeding its practical applications. Herein, a series of Y3– xDyxFe5O12 (x = 0, 0.5, 1.0, 1.5, 3) solid solution crystals was grown by the flux-Bridgman method and single crystals up to 25 mm were obtained. With the introduction of Dy3+, lattice parameters are gradually enlarged from 1.2379 nm (YIG) to 1.2420 nm (DyIG). Typical Dy3+ absorption peaks are observed around 1070, 1265 and 1670 nm. The refractive index decreases from 2.37 (500 nm) to 2.10 (2500 nm) for YIG crystal, and it reduces from 2.47 (500 nm) to 2.16 (2500 nm) for DyIG crystal. The optical bandgaps remain almost unchanged for Dy:YIG crystals. The optical dispersion of the refractive indices was finely fitted by the Wemple and DiDomenico (WDD) and the Sellmeier models, respectively. With the increase of Dy3+ content, the saturation magnetization (M s ) decreases significantly from 23.62 emu/g (YIG) to 5.33 emu/g (DyIG). Small coercive field is persisted for this system, endowing small external magnetic field. These results provide valuable references for the manipulation of rare earths on the properties of magneto-optical crystals, which is beneficial to the design of high-performance garnet crystals for the application of optical switching and non-reciprocal related devices.

A mixed rare-earth iron garnet single crystal of ReYbBiIG for high-performance magneto-optical devices

Mixed rare-earth iron garnet AYbBiIG single-crystals for high-performance optical isolation

Growth and Characterization of Magneto-Optical Single-Crystal Reybbiig with Temperature-Stabilized Faraday Rotation

Bismuth-substituted yttrium iron garnet film/frystal composite for Faraday rotators

Faraday Rotation Spectra Analysis Of Bi-Substituted Mixed Rare-Earth Iron Garnet Crystals In Optical Communication Band

Recent advances of rare earth iron garnet magneto-optical single crystals

Giant reduced magnetic anisotropy in magneto-optical garnet

Study on wideband and temperature properties of TbybBiIg crystal in 1500 similar to 1620nm band

Growth, optical dispersion and magnetic behavior of Dy3+ doped yttrium iron garnet crystals

Growth and characterization of holmium-doped yttrium iron garnet single crystal

Excellent Magnetocaloric Performance in the Carbide Compounds RE2Cr2C3 (RE = Er, Ho, and Dy) and Their Composites

Research of preparing Bi substituted yttrium iron garnet and epoxy magneto-optical hybridized films

Strain-induced magnetic anisotropy of REIG thin films grown on YAG(111) substrates by pulsed laser deposition

Fabrication and performance evaluation of novel transparent ceramics RE:Tb3Ga5O12 (RE = Pr, Tm, Dy) toward magneto-optical application

High Figure of Merit Magneto‐Optical Ce‐ and Bi‐Substituted Terbium Iron Garnet Films Integrated on Si

Dynamic Performance of Magneto-Optical Bi-substituted Rare-Earth Iron Garnet

Faraday-Rotation in Iron Garnet Films Beyond Elemental Substitutions

Multiple spin switching and magnetocaloric effects in orthoferrite Yb0.25Tb0.75FeO3 single crystal

Nanostructure Magneto-Optical Thin Films of Rare Earth (re=gd,tb,dy) Doped Cobalt Spinel by Sol–gel Synthesis

Magnetic Characterization of Zone-Refined Rare-Earth Orthoferrite Crystals Grown by the Optical Floating Zone Method

Rare-earth-mediated Magnetism and Magneto-Optical Kerr Effects in Nanocrystalline CoFeMn0.9RE0.1O4 Thin Films