Abstract:The novel bismuth-substituted rare earth iron garnet films were grown by the modified liquid phase epitaxy (LPE) technique for use as a 45degrees faraday rotator in optical isolators. First, single crystals of Y3Fe5O12(YIG), with a lattice, constant of 1.2378 nm, were grown by means of the Czochralski method. Using YIG instead of the conventional nonmagnetic garnet of Gd3Ga5O12(GGG) as a substrate, a film of BiYbIG was grown by means of the LPE method from Bi2O3-B2O3 fluxes. The structural, magnetic and magneto-optical properties of BiYbIG LPE film/YIG crystal composite were investigated using X-ray diffraction (XRD), electron probe microanalysis (EPMA), vibrating sample magnetometry (VMS) and near-infrared transmission spectrometry. The saturation magnetization 47piM(s) was estimated to be about 1200 G. The Faraday rotation spectrum was measured by the method of rotating analyzer ellipsometry (RAE) with the wavelength varied from 800 to 1700 nm. The resultant Bi0.37Yb2.63Fe5O12 LPE film/YIG crystal composite shows an increased Faraday rotation coefficient due to doping W, ions on the dodecahedral sites of the magnetic garnet without increasing absorption loss, therefore a good magneto-optic figure of merit, defined by the ratio of Faraday rotation and optical absorption loss, can achieved of 21.5 and 30.2degrees/dB at 1300 and 1550 nm wavelengths respectively at room temperature. Since Yb3+ ions and Y3+ ions provide the opposite contributes to the wideband and temperature characteristics of Faraday rotation, the values of Faraday rotation wavelength and temperature coefficients are reduced to 0.06%/nm and 0.007 degrees(.) degreesC(-1) at 1550 nm wavelength respectively.

Growth and Characterization of Magneto-Optical Single-Crystal Reybbiig with Temperature-Stabilized Faraday Rotation

Mixed rare-earth iron garnet AYbBiIG single-crystals for high-performance optical isolation

A mixed rare-earth iron garnet single crystal of ReYbBiIG for high-performance magneto-optical devices

Growth of Ba2Re(Y,Pr)Ru1‐xCuxO Single Crystals in a High Temperature Solution Drop Using an Infrared Imaging System

Bismuth-substituted yttrium iron garnet film/frystal composite for Faraday rotators

Study on wideband and temperature properties of TbybBiIg crystal in 1500 similar to 1620nm band

Research of preparing Bi substituted yttrium iron garnet and epoxy magneto-optical hybridized films

Temperature-independent ferromagnetic resonance shift in Bi-doped YIG garnets through magnetic anisotropy tuning

Enhancing Temperature Stability of Ce: RIG Films Faraday Rotation through Magnetic Sublattice Control

Multiple spin switching and magnetocaloric effects in orthoferrite Yb0.25Tb0.75FeO3 single crystal

Ferromagnetic Resonance Studies of Strain tuned Bi:YIG Films

Relaxor Ferroelectric Characteristics And Temperature-Dependent Domain Structure In A (110)-Cut (Pbmg1/3nb2/3o3)(0.75)(Pbtio3)(0.25) Single Crystal

Temperature And Field Induced Spin Reorientation And Dielectric Properties In Ycr0.88fe0.12o3 Single Crystal

Temperature-induced Spin Reorientation and Magnetization Jump of Rare-Earth Orthoferrite Ho0.5Pr0.5FeO3 Single Crystal

Magnetic phase transition and continuous spin switching in a high-entropy orthoferrite single crystal

Growth and characterization of holmium-doped yttrium iron garnet single crystal

Magnetic Characterization of Zone-Refined Rare-Earth Orthoferrite Crystals Grown by the Optical Floating Zone Method

Effective Faraday Rotator Based on the TbYO3 Crystal with a High Verdet Constant and a High Thermal Conductivity.

Fabrication and performance evaluation of novel transparent ceramics RE:Tb3Ga5O12 (RE = Pr, Tm, Dy) toward magneto-optical application

Spin Reorientation and Giant Low-Temperature Magnetostriction of Polycrystalline NdFe1.9 Compound

Recent advances of rare earth iron garnet magneto-optical single crystals