Abstract:The novel bismuth-substituted rare earth iron garnet films were grown by the modified liquid phase epitaxy (LPE) technique for use as a 45degrees faraday rotator in optical isolators. First, single crystals of Y3Fe5O12(YIG), with a lattice, constant of 1.2378 nm, were grown by means of the Czochralski method. Using YIG instead of the conventional nonmagnetic garnet of Gd3Ga5O12(GGG) as a substrate, a film of BiYbIG was grown by means of the LPE method from Bi2O3-B2O3 fluxes. The structural, magnetic and magneto-optical properties of BiYbIG LPE film/YIG crystal composite were investigated using X-ray diffraction (XRD), electron probe microanalysis (EPMA), vibrating sample magnetometry (VMS) and near-infrared transmission spectrometry. The saturation magnetization 47piM(s) was estimated to be about 1200 G. The Faraday rotation spectrum was measured by the method of rotating analyzer ellipsometry (RAE) with the wavelength varied from 800 to 1700 nm. The resultant Bi0.37Yb2.63Fe5O12 LPE film/YIG crystal composite shows an increased Faraday rotation coefficient due to doping W, ions on the dodecahedral sites of the magnetic garnet without increasing absorption loss, therefore a good magneto-optic figure of merit, defined by the ratio of Faraday rotation and optical absorption loss, can achieved of 21.5 and 30.2degrees/dB at 1300 and 1550 nm wavelengths respectively at room temperature. Since Yb3+ ions and Y3+ ions provide the opposite contributes to the wideband and temperature characteristics of Faraday rotation, the values of Faraday rotation wavelength and temperature coefficients are reduced to 0.06%/nm and 0.007 degrees(.) degreesC(-1) at 1550 nm wavelength respectively.

Effective Faraday Rotator Based on the TbYO3 Crystal with a High Verdet Constant and a High Thermal Conductivity.

Highly Nd3+-doped Y3Al5O12 Crystal Fiber Tip for Laser Thermotherapy.

Design, Growth, and Characterization of High Verdet Constant Magneto-Optical Crystal in Cubic Oxide System Tb2O3/Y2O3/ZrO2 Crystal with Enhanced Laser-Induced Damage Threshold

Design, Growth, and Characterization of High Verdet Constant Magneto-Optical Crystal in Cubic Oxide System Tb 2 O 3 /Y 2 O 3 /ZrO 2 Crystal with Enhanced Laser-Induced Damage Threshold

Mixed rare-earth iron garnet AYbBiIG single-crystals for high-performance optical isolation

Crystal growth and enhanced magneto-optical properties of terbium aluminum gallium garnet crystal for Faraday isolators

Tb 3 Al 3 Ga 2 O 12 : A Novel Visible–Infrared Faraday Crystal Exhibiting a Superior Magneto-Optical Performance

Fabrication and characterizations of a Gadolinium doped terbium gallium garnet crystal for Faraday rotators

Growth and Characterization of Magneto-Optical Single-Crystal Reybbiig with Temperature-Stabilized Faraday Rotation

Study on wideband and temperature properties of TbybBiIg crystal in 1500 similar to 1620nm band

Transparent non-stoichiometric Tb2.45Hf2O7.68 magneto-optical ceramics with high Verdet constant

A mixed rare-earth iron garnet single crystal of ReYbBiIG for high-performance magneto-optical devices

Thermal conductivity versus Yb3+ concentration in Yb:CALGO: A material for high power ultrafast laser

Terahertz magneto-optical effect of wafer-scale La: yttrium iron garnet single-crystal film with low loss and high permittivity

Study on laser-induced damage of TbBiIG crystal at 1064 nm

Fabrication and performance optimization of novel (Tb0.9975R0.0025)3Sc2Al3O12 (R= Pr, Ho, Dy, Eu) magneto-optical transparent ceramics

Optical properties and Faraday magneto-optical effects of highly transparent novel Tb2Zr2O7 fluorite ceramics

Tm-doped crystals for mid-IR optical cryocoolers and radiation balanced lasers

Laser oscillation with low quantum defect in Yb:GdVO4, a crystal with high thermal conductivity.

Bismuth-substituted yttrium iron garnet film/frystal composite for Faraday rotators

Advances of Yb:CALGO Laser Crystals