SrGa12O19: the First Low-Εr Ga-based Microwave Dielectric Ceramic with Anomalous Positive Τf
Yang,Weishuang Fang,Huixing Lin,Jie Li,Huaicheng Xiang,Ying Tang,Lei Li,Liang Fang
DOI: https://doi.org/10.26599/jac.2024.9220947
IF: 11.534
2024-01-01
Journal of Advanced Ceramics
Abstract:Dielectric ceramics with low permittivity (epsilon(r)), high quality factor (Qxf), and near-zero resonant frequency (tau(f)) in the microwave bands are key materials used in fifth/sixth-generation (5G/6G) telecommunication, while tau(f) of most low-epsilon(r) microwave dielectric ceramics is relatively negative. In this work, the first low-epsilon(r) Ga-based ceramic SrGa12O19 with an anomalous positive tau(f) was reported, and the causes of the positive tau(f), intrinsic polarization, and loss mechanism were systematically studied. X-ray diffraction (XRD) and transmission electron microscopy (TEM) revealed that the SrGa12O19 ceramic formed a pure hexagonal magnetoplumbite structure with spinel blocks and rock-salt blocks stacked along the crystallographic c-axis. When sintered at 1430 degrees C, it possessed the optimal microwave dielectric properties of a low epsilon(r) of 14.46, high Qxf of 64,705 GHz, and exceptional positive tau(f) of +55.7 ppm/degrees C, along with a low linear thermal expansion coefficient (alpha(L)) of 11.617 ppm/degrees C. The large positive deviation between epsilon(r) and epsilon(r(C-M)) of 45.31% resulted from the rattling effect of atoms in the rock-salt block. The unique positive tau(f) (+55.7 ppm/degrees C) was governed by the rattling effect, resulting in a positive tau(alpha m) (the temperature coefficient of ion polarizability) of 8.489 ppm/degrees C and a large negative temperature coefficient of permittivity (tau(epsilon)) of -132.864 ppm/degrees C. Phillips-Vechten-Levine (P-V-L) chemical bond theory revealed greater contributions of the spinel block to bond ionicity (f(i), 52.95%), permittivity (epsilon, 55.15%), bond energy (E, 56.87%), and lattice energy (U, 74.88%) than those of the rock-salt block. The intrinsic dielectric properties were analyzed using infrared (IR) reflectivity spectra. The favorable performance of the SrGa12O19 ceramic indicated that it is a novel tau(f) compensator. This selection of compounds with different structural layer combinations provides a new idea for exploring excellent microwave dielectric ceramics.