Abstract:Single-crystal europium iron garnet (EuIG) thin films epitaxially strain-grown on gadolinium gallium garnet (GGG)(100) substrates using off-axis sputtering have strain-induced perpendicular magnetic anisotropy (PMA). By varying the sputtering conditions, we have tuned the europium/iron (Eu/Fe) composition ratios in the films to tailor the film strains. The films exhibited an extremely smooth, particle-free surface with roughness as low as 0.1 nm as observed using atomic force microscopy. High-resolution x-ray diffraction analysis and reciprocal space maps showed in-plane epitaxial film growth, very smooth film/substrate interface, excellent film crystallinity with a small full width at half maximum of 0.012$^{\circ}$ in the rocking curve scans, and an in-plane compressive strain without relaxation. In addition, spherical aberration-corrected scanning transmission electron microscopy showed an atomically abrupt interface between the EuIG film and GGG. The measured squarish out-of-plane magnetization-field hysteresis loops by vibrating sample magnetometry in conjunction with the measurements from angle-dependent x-ray magnetic dichroism demonstrated the PMA in the films. We have tailored the magnetic properties of the EuIG thin films, including saturation magnetization ranging from 71.91 to 124.51 emu/c.c. (increase with the (Eu/Fe) ratios), coercive field from 27 to 157.64 Oe, and the strength of PMA field ($H_\bot$) increasing from 4.21 to 18.87 kOe with the in-plane compressive strain from -0.774 to -1.044%. We have also investigated spin transport in Pt/EuIG bi-layer structure and evaluated the real part of spin mixing conductance to be $3.48\times10^{14} {\Omega}^{-1}m^{-2}$. We demonstrated the current-induced magnetization switching with a low critical switching current density of $3.5\times10^6 A/cm^2$, showing excellent potential for low-dissipation spintronic devices.

Magneto-Optical and Microwave Properties of Lubiig Thin Films Prepared by Liquid Phase Epitaxy Method from Lead-Free Flux

Mixed rare-earth iron garnet AYbBiIG single-crystals for high-performance optical isolation

Giant reduced magnetic anisotropy in magneto-optical garnet

A mixed rare-earth iron garnet single crystal of ReYbBiIG for high-performance magneto-optical devices

Low-damping sub-10-nm thin films of lutetium iron garnet grown by molecular-beam epitaxy

Nanometer thick magneto-optical iron garnet films

Research of preparing Bi substituted yttrium iron garnet and epoxy magneto-optical hybridized films

A New Approach of Preparing Nanocrystalline Bi-YIG Films

Pulsed laser deposition of epitaxial yttrium iron garnet films with low Gilbert damping and bulk-like magnetization

High Figure of Merit Magneto‐Optical Ce‐ and Bi‐Substituted Terbium Iron Garnet Films Integrated on Si

LPE growth of (NdGdBi)3Fe5O12 films with high FOM and high LIDTs at a wavelength of around 1 μm

Bismuth-substituted yttrium iron garnet film/frystal composite for Faraday rotators

Epitaxial growth and magnetic properties of ultraviolet transparent Ga2O3/(Ga1-xFex)2O3 multilayer thin films

Magnetic and magneto-optical properties of Cu-doped Bi,Ga:DyIG and Bi,Al:DyIG films prepared by sol-gel

Magneto-optical epitaxial bismuth-substituted yttrium iron garnet thin films on a diamagnetic substrate for low temperature applications

Supplemental Materials for “ Photo-Spin-Voltaic Effect ”

The Multiferroic Properties of (bi(0.9)ba(0.1))(fe(0.95)mn(0.05))o(3) Films

Piezoelectric and magneto-optical effect of lanthanum-doped bismuth ferrite films on silicon substrate

Magneto-Optical and Optical Properties of Gdfe Films

Single-crystal epitaxial europium iron garnet films with strain-induced perpendicular magnetic anisotropy: structural, strain, magnetic, and spin transport properties

Lattice-tunable substituted iron garnets for low-temperature magnonics