Abstract:We have investigated the Faraday rotation of in-plane magnetized bismuth - substituted ferrite garnet films grown by liquid phase epitaxy on (100) oriented gadolinium gallium garnet substrates. The Faraday spectra were measured for photon energies between 1.7 - 2.6 eV. To interprete the spectra, we use a model based on two electric dipole transitions, one tetrahedral and one octahedral. Furthermore, the Faraday rotation sensitivity was measured at 2.3 eV, and found to be in good agreement with the theoretical predicitions. In particular, we find that the sensitivity increases linearly with the bismuth content and nonlinearly with the gallium content.

Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to study the Faraday rotation characteristics and their sensitivity of bismuth - substituted ferrite garnet films (Bi:FG), especially the films grown on (100) - oriented substrates. Specifically, the authors hope to understand the following aspects through experimental and theoretical models:

1. **Faraday Rotation Spectrum**: The Faraday rotation spectra of bismuth - substituted ferrite garnet films magnetized in - plane were measured, and these spectral features were explained. The photon energy range was from 1.7 to 2.6 eV (corresponding to wavelengths from 730 to 480 nm). To explain these spectra, they used a simple model based on two electric dipole transitions, one located at the tetrahedral site and the other at the octahedral site.

2. **Sensitivity Analysis**: The Faraday rotation sensitivity at 2.3 eV was measured, and its consistency with theoretical predictions was verified. In particular, the relationships of the sensitivity increasing linearly with bismuth content and changing non - linearly with gallium content were studied.

3. **Material Property Optimization**: By adjusting the chemical composition (especially the contents of bismuth and gallium), the magneto - optical response of the films was optimized to improve their application potential in magneto - optical imaging and detection.

### Main Research Contents

- **Sample Preparation**: A series of bismuth - and gallium - substituted ferrite garnet films were grown on (100) - oriented gadolinium gallium garnet (GGG) substrates by liquid - phase epitaxy (LPE) technology, and their chemical compositions were characterized.

- **Faraday Rotation Spectrum Measurement**: The Faraday rotation spectra of different samples were measured and fitted by a theoretical model. The formula is as follows:
\[
\Theta_{\text{sat}}^F=\frac{\pi e^2\omega^2}{nmc}\sum_i N f_i\left[\frac{(ω_i + Δ_i)^2 - ω^2 - Γ_i^2}{[(ω_i + Δ_i)^2 - ω^2 + Γ_i^2]^2 + 4ω^2Γ_i^2}-\frac{(ω_i - Δ_i)^2 - ω^2 - Γ_i^2}{[(ω_i - Δ_i)^2 - ω^2 + Γ_i^2]^2 + 4ω^2Γ_i^2}\right]
\]
where \(ω_i\) is the resonance energy, \(f_i\) is the oscillation intensity, \(Γ_i\) is the half - width of the transition, \(e\) and \(m\) are the electron charge and mass respectively, and \(N\) is the active ion density.

- **Sensitivity Measurement**: The Faraday rotation sensitivity \(S\) was defined and the effects of bismuth and gallium were separated:
\[
S = \frac{dΘ_F}{dH_z}=\frac{Θ_{\text{sat}}^F}{H_a}
\]
\[
S_{\text{Bi}} = S\frac{(1 - 0.7z)}{(1 - z_d/3)(1 - z_a/2)}
\]
\[
S_{\text{Ga}}=\frac{S}{x}
\]

### Conclusion

The research shows that the Faraday rotation sensitivity of bismuth - substituted ferrite garnet films increases linearly with bismuth content and changes non - linearly with gallium content. These results are helpful for optimizing the application performance of these materials in magneto - optical imaging and detection.