Abstract:Cu matrix composites have received increased attention in a wide industrial area because of their excellent mechanical properties and good electrical and thermal conductivity. However, the addition of general ceramic reinforcements often leads to a marked reduction in electrical conductivity for Cu matrix composites. In this study, the ZrB 2 -reinforced Cu composites have been developed to overcome this drawback since these metal borides possess relatively high electrical conductivity. The 5 wt.% ZrB 2 /Cu composites were prepared using hot-pressed sintering techniques at varying temperatures from 760 to 920°C. The influence of sintering temperature on the microstructure, relative density, and mechanical and electrical properties was examined. The results of the SEM observation show that ZrB 2 particles are seamlessly integrated into the Cu matrix for all ZrB 2 /Cu composites. The average grain size of the Cu matrix increases from 360 to 980 nm with the increase of the sintering temperature. The increase in sintering temperature also leads to the surface porosity decrease from 1.4 to 0.4%. The relative density and electric conductivity of the composites increase at the same time as the sintering temperature increases. However, microhardness increases and decreases, with a maximum value of 92 HV0.2 achieved at 840°C. The elastic modulus and nanohardness maps determined from the nanoindentation indicate that the reinforced ZrB 2 particles demonstrate the highest values for elastic modulus (340–500 GPa) and nanohardness (30–48 GPa). At the same time, the Cu matrix possesses a modulus of 100–200 GPa and nanohardness of about 10 GPa. TEM observation confirmed that the sintering temperature exhibits little influence on the interface reaction between ZrB 2 and Cu. Both sharp interface and interface with amorphous transition layer are observed. The variation of microhardness is mainly due to the strengthening of grain refinement and to the mismatch of the thermal expansion coefficients. The above results can provide further insights into the deeper understanding of the role of sintering temperature during hot-pressed sintering.

Mechanical and Thermal Properties of ZrC/ZTA Composites Prepared by Spark Plasma Sintering

Influence of Zrc Content on the Elevated Temperature Tensile Properties of Zrcp/W Composites

Effects of ZrC content on the microstructure and mechanical property of ZrC/ZTA composites consolidated by hot pressing

Effect of Sintering Temperature on the Microstructure and Properties of High-Strength and Highly Conductive 5 wt.% ZrB2/Cu Composite

Mechanical and thermal properties of Al 2O 3-ZrO 2 composite ceramics at cryogenic temperatures

Effect of TZP nanoparticles synthesized by RCVD on mechanical properties of ZTA composites sintered by SPS

Microstructures and Enhanced Mechanical Properties of (Zr, Ti)(C, N)-Based Nanocomposites Fabricated by Reactive Hot-Pressing at Low Temperature

Study on Mechanical Properties of Hot Pressing Sintered Mullite-Zro2 Composites with Finite Element Method

Effects of ZrB2 on Mechanical Properties of Al2O3-ZrB2-SiC Composite Ceramics at Room Temperature

Effect of sintering temperature and holding time on the microstructure and mechanical properties of ZrB2–SiCw composites

Microstructure and Mechanical Properties of Hot-Pressed Al2O3–mullite–ZrO2–SiC Composites

Correlation between phase content and mechanical properties of SiCw- ZTA composites sintered by SPS

Microstructure and Mechanical Properties of ZTA Composites Fabricated by Oscillatory Pressure Sintering

Microstructure and mechanical properties of Zn based composites reinforced by Ti3AlC2

Preparation and Characterization of ZrB 2 -Sic Ultra-High Temperature Ceramics by Microwave Sintering

Mechanical properties and microstructure of spark plasma sintered Al2O3-SiCw-Si3N4 composite ceramic tool materials

Microstructure and mechanical properties of TiC reinforced TZM composites prepared by spark plasma sintering

Toughening Mechanisms of ZTA Ceramics at Cryogenic Temperature (77 K)

Microstructure, Mechanical, and Thermal Properties of in Situ-Synthesized (zrb2+sic)/zr2[al(si)]4c5 Composites

Microstructure and mechanical properties of dense ZTA ceramics with high Cr2O3 solution

Temperature‐dependent mechanical and oxidation behavior of in‐situ formed ZrN/ZrO2‐containing Si3N4‐based composite