Improvement of soft magnetic properties of a Nanoperm-type Fe-Hf-B nanocrystalline alloy upon surface crystallization inhibition by Cu addition
Licheng Wu,Yanhui Li,Aina He,Zhengwang Zhu,Haifeng Zhang,Wei Zhang
DOI: https://doi.org/10.1016/j.intermet.2023.108040
IF: 4.075
2023-09-01
Intermetallics
Abstract:Nanoperm-type alloy ribbons suffer from surface crystallization during melt spinning, which degrades their magnetic properties after annealing and limits their commercial application. Here, we investigate the effects of Cu addition on the structure and magnetic properties of a surface-textured Fe 87-x Hf 5 B 8 Cu x alloy. Adding Cu (1 ≤ x ≤ 2) removes the surface coarse grains in the free surface of the melt-spun precursor, while induces the precipitation of large amounts of the α-Fe nanoparticles with ∼3 nm in size, which contributes a homogeneous ultrafine structure and improved magnetic softness after annealing. The grain size, coercivity, saturation magnetic flux density, and effective permeability at 1 kHz of the Fe 86 Hf 5 B 8 Cu 1 nanocrystalline alloy are 13.3 nm, 6.6 A/m, 1.68 T, and 23000, respectively, whereas these are 16.0 nm, 16.8 A/m, 1.70 T, and 15000, respectively, for the Fe 87 Hf 5 B 8 alloy. The Cu-improved effect is mainly attributed that Cu induces heterogeneous nucleation of the α-Fe phase to strengthen the competitive growth among grains.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering