Abstract:In this study, the initial electrical properties, positive gate bias stress (PBS), and drain current stress (DCS)-induced instabilities of amorphous indium gallium zinc oxide (a-IGZO) thin-film transistors (TFTs) with various active layer thicknesses (TIGZO) are investigated. As the TIGZO increased, the turn-on voltage (Von) decreased, while the subthreshold swing slightly increased. Furthermore, the mobility of over 13 cm²&middot;V&minus;1&middot;s&minus;1 and the negligible hysteresis of ~0.5 V are obtained in all of the a-IGZO TFTs, regardless of the TIGZO. The PBS results exhibit that the Von shift is aggravated as the TIGZO decreases. In addition, the DCS-induced instability in the a-IGZO TFTs with various TIGZO values is revealed using current&ndash;voltage and capacitance&ndash;voltage (C&ndash;V) measurements. An anomalous hump phenomenon is only observed in the off state of the gate-to-source (Cgs) curve for all of the a-IGZO TFTs. This is due to the impact ionization that occurs near the drain side of the channel and the generated holes that flow towards the source side along the back-channel interface under the lateral electric field, which cause a lowered potential barrier near the source side. As the TIGZO value increased, the hump in the off state of the Cgs curve was gradually weakened.

Self-Heating Stress-Induced Severe Humps in Transfer Characteristics of Amorphous InGaZnO Thin-Film Transistors

Competition Between Heating and Cooling During Dynamic Self-Heating Degradation of Amorphous InGaZnO Thin-Film Transistors

Roles of Hot Carriers in Dynamic Self-Heating Degradation of a-InGaZnO Thin-Film Transistors

Fluorination-mitigated High-Current Degradation of Amorphous InGaZnO Thin-Film Transistors

Investigation of an Anomalous Hump Phenomenon in Via-Type Amorphous In-Ga-Zn-O Thin-Film Transistors under Positive Bias Temperature Stress

Investigating the Back-Channel Effect and Asymmetric Degradation under Self-Heating Stress in Large Size A-Ingazno TFTs

Abnormal Threshold Voltage Shift Caused by Trapped Holes under Hot-Carrier Stress in A-Igzo TFTs

Temperature-Dependent Instability of Bias Stress in InGaZnO Thin-Film Transistors

Drain Current Stress-Induced Instability in Amorphous InGaZnO Thin-Film Transistors with Different Active Layer Thicknesses

Temperature-dependent bias-stress-induced electrical instability of amorphous indium-gallium-zinc-oxide thin-film transistors

Thermal Annealing Improved Stability of Amorphous InGaZnO Thin-Film Transistors Under AC Bias Stresses

Temperature Dependent Anomalous Threshold Voltage Modulation of a-IGZO TFT by Incorporating Variant Gate Stresses

Bi-directional threshold voltage shift of amorphous InGaZnO thin film transistors under alternating bias stress

Investigation of a Hump Phenomenon in Back-Channel-Etched Amorphous In-Ga-Zn-O Thin-Film Transistors under Negative Bias Stress

Origin of light instability in amorphous IGZO thin-film transistors and its suppression

Asymmetry Degradation Behavior Under Forward and Backward Overlap Dynamical Stress in Large-Size Amorphous InGaZnO TFT

P‐1.5: Dynamic Current Stress‐Induced Instabilities of A‐ingazno TFTs

Degradation Behavior of Etch-Stopper-Layer Structured A-Ingazno Thin-Film Transistors under Hot-Carrier Stress and Illumination

Abnormal Bias Instabilities Induced by Lateral H2O Diffusion into Top-Gate Insulator of A-Ingazno Thin-Film Transistors

Oxygen interstitial creation in a-IGZO thin-film transistors under positive gate-bias stress

The Influence of Annealing Temperature on Amorphous Indium‐Zinc‐Tungsten Oxide Thin‐Film Transistors