Investigation of Microstructure Evolution and Mechanical Properties of Multi-Precipitation Ni–Co Base Superalloys

Yu Li,Zhenjun Hong,Binggang Liu,Xiaoshuai Jia
DOI: https://doi.org/10.1016/j.msea.2020.140333
IF: 6.044
2020-01-01
Materials Science and Engineering A
Abstract:The microstructure evolution and mechanical properties were investigated in a multi-precipitation Ni-Co base superalloy system with different chemical compositions (wt. %) of Ni-30-Co-33-C-0.02 (1#) and Ni-28.5-Co-34.5-C-0.01 (2#). The interaction of multi-precipitates and its influence on the creep behavior were studied in correlation with the evolution of deformed microstructure. The multi-precipitates mainly consist of gamma '-Ni3Al phase, beta-NiAl phase, carbides, and eta phase. After a long term aging, both of the beta and gamma ' phase possess a strong thermal stability in the two superalloys, while the number density of eta precipitates has increased a lot (volume fraction: 0.02%-0.21%) in the 2# Ni-Co alloys compared with that in the 1# Ni-Co alloys. The room temperature mechanical properties of both Ni-Co alloys almost remain stable such as ultimate tensile strength (1260-1280 MPa) and total elongation (22-24%) even after a long aging time of 1500 h. However, different from the stress-free aging process, the gamma ' precipitate in the 2# Ni-Co alloy shows a higher rafting rate compared with that in the 1# Ni-Co alloy after the creep (903 K, 450 MPa) for 500 h. Thus, the 2# Ni-Co alloy exhibits a significantly higher creep strain rate and an advanced accelerating creep stage than the 1# Ni-Co alloy. The differences of the creep properties are mainly attributed to a change in deformation mechanism from dislocation gliding to dislocation climbing over the rafted gamma ' phase during the steady-state stage. A high stacking fault energy (SFE) of the matrix results in strong stress concentration and dislocation network formation in the gamma/gamma ' interfaces, contributing to an accelerated creep strain rate of the 2# Ni-Co alloy. In contrast, sustainable precipitation hardening from spherical MC carbides can delay the steady-state stage to a very long life until 1500 h in the 1# Ni-Co alloy.
What problem does this paper attempt to address?