Abstract:Abstract Mullite porous ceramics with high porosity and good mechanical properties were prepared by foaming method combined with gel casting process using kaolin and alumina as main raw materials and sodium polyoxyethylene ether sulfate as foaming agent. The effects of sintering process and magnesium oxide content on the microstructure and properties of mullite porous ceramics were investigated. The studies show that: With the addition of magnesium oxide, the amount of mullite produced and the compactness of the sample will increase. At this time, the microscopic morphology of mullite is needle-like and prismatic, and the mechanical properties are better. and the pore size distribution gradually tends to be between 0.1-0.2mm and 0.2-0.3mm. The addition of magnesium oxide, The amount of mullite phase increased, the densification degree of the sample increased, and the acicular and prismatic mullite phases with good mechanical properties were mainly formed, and the porosity of mullite porous ceramics decreased and the compressive strength increased. The pore size distribution gradually tends to be between 0.1-0.2mm and 0.2-0.3mm. As the sintering temperature increases, the porosity of mullite porous ceramics decreases and the compressive strength increases. With the extension of the holding time, the amount of mullite phase generated increases, the porosity remains basically unchanged, and the compressive strength increases.

Phase Formation, Microstructure Development, and Mechanical Properties of Kaolin‐based Mullite Ceramics Added with Fe2O3

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

Influence of CaO content by mass in sintering aid and sintering temperature on the properties of Al2O3-based microwave ceramic materials

Modification of liquid phase and microstructure of sintered mullite by different additives

Effect of particle size of associated rare earth kaolin powder on the sintering and properties of synthetic mullite

Phase evolution and sintering characteristics of porous mullite ceramics produced from the flyash-Al(OH)3 coating powders

Preparation of Mullite from Low-grade Kaolin

Effect of the different additives on the fabrication of porous kaolin-based mullite ceramics

Effect of Fe2O3 addition on sintering behavior of cordierite ceramic obtained by solid-state sintering method

Low-temperature Densification and Mechanical Properties of Monolithic Mullite Ceramic

Significantly improved mechanical properties of mullite ceramics by adding AlOOH with different sizes and morphologies

The Fabrication of Porous Mullite Ceramics Based on the Different Sizes of Aluminum Hydroxide

Microstructure evolution and mechanical behavior of a mullite fiber heat‐treated from 1100 to 1300°C

Preparation and properties of porous mullite-based ceramics fabricated by solid state reaction

Effect Of Y2o3 On Property Of Mullite Ceramic Enhanced By Andalusite

Influence of MgO on Properties and Microstructure of Mullite Ceramics Synthesized from Coal Fly Ash

Effects of AlF3 and MoO3 on properties of Mullite whisker reinforced porous ceramics fabricated from construction waste

Effect of Alumina Addition on the Properties of Corundum-Mullite Ceramic Matrix

Effect Of Sintering Process On Micro-structure And Properties Of Mullite Porous Ceramics Containing magnesium oxide

Physico-Mechanical and Microstructure Characteristics of Porous Mullite Ceramics

Effects of Composite Sintering Additives: Al(OH)3+Y2O3+CaF2 on the Performance of Porous Mullite Oxide-Bonded SiC Ceramics