Abstract:This study was aimed to investigate the effect of steel, polypropylene (PP), and hybrid (steel + PP) fibers on high-temperature mechanical properties of reactive powder concrete (RPC). The mechanical properties considered are cubic compressive strength, axial or prismatic compressive strength, split-tensile strength, flexural strength, elastic modulus, peak strain, and stress-strain behavior. The strength recession due to high temperature was investigated at micro level by scanning electron microscope, energy dispersive X-ray spectroscopy, X-ray diffraction, mercury intrusion porosity, thermogravimetric, and differential scanning calorimetry analyses. The high-temperature tests were carried out at target temperatures of 120, 300, 500, 700, and 900 °C. The hot-state compressive strength of RPC started to decrease at 120 °C; however, a partial recovery at 300 °C and a gradual decrease above 300 °C were observed. The degradation of split-tensile strength, flexural strength, and elastic modulus were gradual with increasing temperature despite the effect of different fibers. Whereas, the peak strain was gradually increasing up to 700 °C. However, after 700 °C, it remained unchanged. Steel fiber reinforced RPC (SRPC) and hybrid fiber reinforced RPC (HRPC) showed a ductile behavior. PP fiber reinforced RPC (PRPC) showed a quite brittle behavior up to 300 °C; however, further heating made the microstructure porous and it became ductile too. Overall the performance of SRPC and HRPC were superior to PRPC because of higher modulus of elasticity, higher strength, and better fire resistance of steel fibers. Fiber reinforced RPC was found to have better fire resistance than traditional types of concrete based on comparative studies with the provisions of design codes and earlier research. The constitutive equations developed can be utilized in computer programs for structural design of RPC structures exposed to fire.

Modeling the Fire Response of Reactive Powder Concrete Beams with Due Consideration to Explosive Spalling

Experimental Study on the Spalling Strength of Fiber Reactive Powder Concrete

Experimental Research the Shearing Performance of Grading-Fiber Reinforced Reactive Powder Concrete

Experimental Study and Analytical Model of Concrete Cover Spalling Induced by Steel Corrosion

Experimental research on seismic behavior of concrete-filled reactive powder concrete tubular columns

Analysis of the Dynamic Response in Blast-Loaded CFRP-Strengthened Metallic Beams

Experimental Investigation and Numerical Simulation on the Blast Resistance of Reactive Powder Concrete Subjected to Blast by Embedded Explosive

Dynamic Behavior of Reactive Powder Concrete in Split Hopkinson Pressure Bar Testing

The Influence of Spalling on the Fire Resistance of Rc Structures

Numerical Simulation of Steel-Reinforced Reactive Powder Concrete Beam Based on Bond-Slip

Spallation Mechanism of RC Slabs under Contact Detonation

A Novel Dynamic Cavity Expansion Model to Predict the Resistance of Reactive Powder Concrete (RPC) Against Projectile Impact

A close look at fire-induced explosive spalling of ultra-high performance concrete: from materials to structures

Finite Element Modeling of Reinforced Concrete Beams Exposed to Fire

Numerical Investigation of Fire-Induced Spalling of Normal Strength Concrete

PREDICTION OF DEBRIS LAUNCH VELOCITY OF REINFORCED CONCRETE SLAB SUBJECTED TO INTERNAL BLAST LOADING

The Effect on Dynamic Properties of Reactive Powder Concrete under High Temperature Burnt and Its Micro-Structure Analysis

Experiment and validation of local bearing capacity for reactive powder concrete confined with high-strength spirals

Effect of Fibers on High-Temperature Mechanical Behavior and Microstructure of Reactive Powder Concrete

Modeling the Behavior of Insulated FRP-Strengthened Reinforced Concrete Beams Exposed to Fire

Concrete Spalling Behavior and Damage Evaluation of Concrete Members with Different Cross-sectional Properties under Contact Explosion