Abstract:Composite mechanical joints are extensively used and becoming crucial components for primary and secondary structures in industry. Considerable efforts have been contributed to the failure behavior of resin matrix laminate composite bolt joint, but few ones refer to carbon matrix woven composites. In current work, a comprehensive experimental and numerical research on the failure behavior for satin woven carbon/carbon composites under pin-loading, which is the typical loading case for mechanical joint, was presented. Seven types of specimens with different configuration were tested to evaluate the influence of the geometry on the failure modes. The testing results stated that, with the increasing of width-to-hole diameter ratio (W/D) and edge distance-to-hole diameter ratio (E/D), the net tension and shear out failure transformed into the bearing failure respectively, while hole diameter-to-thickness ratio (D/t) hardly affect the failure mode. For a further exploration for damage mechanism of the acceptable bearing failure in engineering, damage accumulation and evolution were assessed combining numerical simulation and acoustic emission monitoring. In view of the complexity of satin woven framework, the hierarchical multiscale numerical strategy from micro-to macro-level was proposed to obtain the material mechanical performance. In order to acquire reliable prediction and consider the effects of the uncertainty sources on composite properties, the model geometry reconstruction was performed using X-ray tomography. Meanwhile, the fiber and void random distributions were determined via the Random Sequential Adsorption algorithm. The Murakami-Ohno damage theory was adopted to characterize the damage propagation. It is concluded that, the numerical prediction agreed with the testing results reasonably well, and the main damage mechanism during the bearing failure included matrix cracking, yarns pulling-out and yarns fracture matching various amplitude ranges of acoustic emission signals.

Failure Behavior Of Plain Weave Fabric Composite With Bolted Joints

Progressive failure analysis of woven and non‐woven CFRP composite/steel bolted joints

Parametric study on the load-carrying capacity of plain-woven composites hybrid bonded-bolted joints

Experimental investigations of bolted, adhesively bonded and hybrid bolted/bonded single-lap joints in composite laminates

Experimental study of bonded, bolted, and hybrid braided CFRP joints with different stacking sequences and lapping patterns

Multiaxial failure mechanism of 3D triple-twill warp-lining woven composites

A Comparative Study on Interlaminar Properties of L-shaped Two-Dimensional (2D) and Three-Dimensional (3D) Woven Composites

Numerical and experimental investigation on the load‐bearing performance of plain‐woven composites hybrid bonded‐bolted joints

Tensile properties of multilayered biaxial weft knitted fabric reinforced composite material

Study on the Bolt-Pin Joint Structure of Carbon Fabric Composites

Analysis on the Turning Point of Dynamic In-Plane Compressive Strength for a Plain Weave Composite

Experimental Investigation of Double-Lap Bolted Composite Joints with Different Outer Plates Subjected to Bending Loads

EXPERIMENTAL INVESTIGATION ON THE TENSILE STRENGTH OF COMPOSITE LAMINATES CONTAINING OPEN AND FILLED HOLES

Micro-XCT Characterization and Numerical Analysis of Bending Damage Mechanism in Carbon Fiber Plain, Twill and Winding Composite Tubes

Effect of triaxial woven fabric on bending properties of unidirectional composites

Experimental investigation on the effects of fabric architectures on mechanical and damage behaviors of carbon/epoxy woven composites

Effect of Crossing Warp Arrangements on Delamination Resistance of 3D Woven Composite T-joints under In-plane Tensile Loading

Experimental and Multiscale Numerical Investigation on Failure Behavior of Satin Woven Carbon/carbon Composites Subjected to Pin-Loading

Flexural Failure Mechanism of Bamboo Composite Plates with Different Construction Technologies and Tectonic Patterns

Study on intralaminar crack propagation mechanisms in single- and multi-layer 2D woven composite laminate

Tensile tests and strength estimation for double-lap single-bolt j oints in T800 carbon fiber reinforced composites