Abstract:We have previously developed silicon-based light-emitting devices (LEDs) with luminescent erbium (Er)-doped TiO2 (TiO2:Er) films [Yang et al., Appl. Phys. Lett. 100, 031103 (2012)]. In an LED therein, the TiO2:Er film is sandwiched between the ITO film and heavily boron-doped p-type silicon (p+-Si). In this work, we have investigated the electroluminescence (EL) from two LEDs with the TiO2:Er films annealed at 650 and 850 °C, respectively. It is revealed that between the TiO2:Er film and p+-Si, there is an intermediate silicon oxide (SiOx, x ≤ 2) layer and its thickness increases from ∼4 to 8 nm with the increase of annealing temperature from 650 to 850 °C. Interestingly, the thickness of the intermediate SiOx layer is found to exhibit a profound impact on the EL from the LED with the TiO2:Er film on p+-Si. The EL from the LED with the 650 °C-annealed TiO2:Er film is activated only under the forward bias with the positive voltage connecting to the p+-Si substrate. Such EL consists of the oxygen-vacancy-related emissions from TiO2 host and the characteristic visible and ∼1540 nm emissions from the Er3+ ions, while the EL from the LED with the 850 °C-annealed TiO2:Er film can only be enabled by the reverse bias with the negative voltage applied on the p+-Si substrate. Such EL features only the visible and ∼1540 nm emissions from the Er3+ ions. The difference in the EL behaviors of the two LEDs as mentioned above is found to be ascribed to the different electrical conduction mechanisms.

Voltage-Tunable And Two-Peak Electroluminescence Of Porous Silicon In Persulphate Solution

Two-peak Electroluminescence of Porous Silicon in Persulphate Solution

Mechanism of Voltage Tunable Electroluminescence of Porous Silicon

Quantum confinement effect in electroluminescent porous silicon

Two kinds of electroluminescence from poroussilicon in electrolyte solutions

Electroluminescence from Tio2/P(+)-Si Heterostructure

Photoluminescence of oxidized porous silicon under UV-light illumination

Sensitized Photoluminescence of Erbium Silicate Synthesized on Porous Silicon Framework

Two-peak Photoluminescence and Light-Emitting Mechanism of Porous Silicon

Optoelectric Characteristics of Porous Silicon Using A Conducting Polymer

Electroluminescence from Silicon-Based Light-Emitting Devices with Erbium-Doped TiO2 Films Annealed at Different Temperatures

The Influence of Microstructure on Optical Properties of Porous Silicon

Electroluminescence of Silicon-Rich Silicon Nitride Light-Emitting Devices

The Optical Properties of Porous Silicon Produced by Metal-Assisted Anodic Etching

A Blue Shift Followed by a Red Shift of the Photoluminescence Spectra for Porous Silicon Treated Alternatively by Chemical Etching and Laser Illumination

Electroluminescence from Sno2/P(+)-Si Heterostructured Light-Emitting Device: Enhancing Its Intensity Via Capping A Tio2 Film

Intense And Stable Blue-Violet Emission From Porous Silicon Modified With Alkyls

A Way To Obtain Visible Blue Light Emission In Porous Silicon

Luminescent and Structural Properties of Electron-Irradiated Silicon Light-Emitting Diodes with Dislocation-Related Luminescence

Color-tunable Electroluminescence from Eu-doped TiO_2/p^+-Si Heterostructured Devices: Engineering of Energy Transfer

Studies on the electroluminescence of porous silicon in formic acid-sodium formate solution at positive biases