Abstract:A wire arc additive manufacturing system, based on cold metal transfer technology, was utilized to manufacture the Al-Mg alloy walls. ER5556 wire was used as the filler metal to deposit Al-Mg alloys layer by layer. Based on the orthogonal experiments, the process parameters of the welding current, welding speed and gas flow, as well as interlayer residence time, were adjusted to investigate the microstructure, phase composition and crystal orientation as well as material properties of Al-Mg alloyed additive. The results show that the grain size of Al-Mg alloyed additive becomes smaller with the decrease of welding current or increased welding speed. It is easier to obtain the additive parts with better grain uniformity with the increase of gas flow or interlayer residence time. The phase composition of Al-Mg alloyed additive consists of α-Al matrix and γ (Al12Mg17) phase. The eutectic reaction occurs during the additive manufacturing process, and the liquefying film is formed on the α-Al matrix and coated on the γ phase surface. The crystal grows preferentially along the <111> and <101> orientations. When the welding current is 90 A, the welding speed is 700 mm/min, the gas flow is 22.5 L/min and the interlayer residence time is 5 min, the Al-Mg alloy additive obtains the highest tensile strength. Under the optimal process parameters, the average grain size of Al-Mg alloyed additive is 25 μm, the transverse tensile strength reaches 382 MPa, the impact absorption energy is 26 J, and the corrosion current density is 3.485 × 10−6 A·cm−2. Both tensile and impact fracture modes of Al-Mg alloyed additive are ductile fractures. From the current view, the Al-Mg alloys manufactured by WAAM-CMT have a better performance than those produced by the traditional casting process.

Microstructures and Properties of Wire-Arc Additively Manufactured 5356 Aluminium Alloy Protected by Different Proportions of Nitrogen and Argon

Comparative study on the microstructures and properties of wire+arc additively manufactured 5356 aluminium alloy with argon and nitrogen as the shielding gas

Effect of N2 content in shielding gas on formation quality and microstructure of high nitrogen austenitic stainless steel fabricated by wire and arc additive manufacturing

Influence of shielding gas nitrogen content on the microstructure and mechanical properties of Cu-reinforced maraging steel fabricated by wire arc additive manufacturing

Microstructure and mechanical properties of wire arc additively manufactured 205A high strength aluminum alloy: The comparison of as-deposited and T6 heat-treated samples

Microstructures and Properties of Al-Mg Alloys Manufactured by WAAM-CMT

Influence of Arc Length Correction on Microstructure, Mechanical Properties, and Defect Formation of Wire-Arc Additive Manufactured 5356 Alloy

Microstructure and Mechanical Properties of Welding Metal with High Cr-Ni Austenite Wire Through Ar-He-N-2 Gas Metal Arc Welding

Microstructures and Mechanical Properties of Al–Zn–Mg Aluminium Alloy Samples Produced by Wire + Arc Additive Manufacturing

Tensile, Fatigue Properties and Their Anisotropies of Al-Mg Alloy Fabricated by Wire-Arc Additive Manufacturing

The heterogeneous band microstructure and mechanical performance in a wire + arc additively manufactured 2219 Al alloy

Microstructures and Mechanical Properties of Wire Arc Additive Manufactured 5183-Al: Influences of Deposition Dimensions

Effect of N2- and CO2-Containing Shielding Gases on Composition Modification and Carbonitride Precipitation in Wire Arc Additive Manufactured Grade 91 Steel

Microstructure and mechanical properties of twin wire and arc additive manufactured Ni3Al-based alloy

Microstructure evolution and mechanical properties of wire-arc-additively manufactured Al–Cu–Mg–Ag alloy

Effect of Gas Protection on Form and Microstructure of Wire Arc Additive Manufactured WE43 Magnesium Alloy

Microstructural Evolution and Mechanical Properties of 2219 Aluminum Alloy Deposited by Wire and Arc Additive Manufacturing

Effect of nitrogen content on microstructure and mechanical properties of duplex stainless steels via wire arc additive manufacturing

Effects of Location on the Microstructure and Mechanical Properties of Cu-8Al-2Ni-2Fe-2Mn Alloy Produced Through Wire Arc Additive Manufacturing

Microstructure and properties research of Al-Zn-Mg-Cu alloy with high strength and high elongation fabricated by wire arc additive manufacturing

Influence of Arc Mode on the Microstructure and Mechanical Properties of 5356 Aluminum Alloy Fabricated by Wire Arc Additive Manufacturing