Abstract:A wire arc additive manufacturing system, based on cold metal transfer technology, was utilized to manufacture the Al-Mg alloy walls. ER5556 wire was used as the filler metal to deposit Al-Mg alloys layer by layer. Based on the orthogonal experiments, the process parameters of the welding current, welding speed and gas flow, as well as interlayer residence time, were adjusted to investigate the microstructure, phase composition and crystal orientation as well as material properties of Al-Mg alloyed additive. The results show that the grain size of Al-Mg alloyed additive becomes smaller with the decrease of welding current or increased welding speed. It is easier to obtain the additive parts with better grain uniformity with the increase of gas flow or interlayer residence time. The phase composition of Al-Mg alloyed additive consists of α-Al matrix and γ (Al12Mg17) phase. The eutectic reaction occurs during the additive manufacturing process, and the liquefying film is formed on the α-Al matrix and coated on the γ phase surface. The crystal grows preferentially along the <111> and <101> orientations. When the welding current is 90 A, the welding speed is 700 mm/min, the gas flow is 22.5 L/min and the interlayer residence time is 5 min, the Al-Mg alloy additive obtains the highest tensile strength. Under the optimal process parameters, the average grain size of Al-Mg alloyed additive is 25 μm, the transverse tensile strength reaches 382 MPa, the impact absorption energy is 26 J, and the corrosion current density is 3.485 × 10−6 A·cm−2. Both tensile and impact fracture modes of Al-Mg alloyed additive are ductile fractures. From the current view, the Al-Mg alloys manufactured by WAAM-CMT have a better performance than those produced by the traditional casting process.

Influence of Arc Length Correction on Microstructure, Mechanical Properties, and Defect Formation of Wire-Arc Additive Manufactured 5356 Alloy

Enhanced High-Temperature Strength and Ductility of Wire Arc Additive Manufactured Al-Ce-Mg Alloys with Fine Α-Al/al11ce3 Eutectics

Influence of Arc Length Correction on Friction and Wear Characteristics of Wire-Arc Additive Manufactured AA 5356 Alloy

Microstructure and mechanical properties of wire arc additively manufactured 205A high strength aluminum alloy: The comparison of as-deposited and T6 heat-treated samples

Influence of Arc Mode on the Microstructure and Mechanical Properties of 5356 Aluminum Alloy Fabricated by Wire Arc Additive Manufacturing

Improving mechanical properties of wire arc additively manufactured AA2196 Al–Li alloy by controlling solidification defects

Microstructural and Defect Evolution during WAAM Resulting in Mechanical Property Differences for AA5356 Component

Investigate the effect of arc characteristic on the mechanical properties of 5A56 Al alloy in CMT arc additive manufacturing

Minimizing porosity and optimizing microstructure of hot-wire arc additive manufactured Al-Cu-Mg-Ag alloy for strength increment

Structure Formation and Mechanical Properties of Wire Arc Additively Manufactured Al4043 (AlSi5) Components

Effect of Deposition Strategies on Microstructures, Defects and Mechanical Properties of 5356 Aluminum Alloy by Wire Arc Additive Manufacturing

Comparative Study on Wire-Arc Additive Manufacturing and Conventional Casting of Al–Si Alloys: Porosity, Microstructure and Mechanical Property

Surface Characteristics, Microstructural, and Tribological Behavior of Wire Arc Additive Manufactured Aluminum-5356 Alloy

Microstructures and Properties of Al-Mg Alloys Manufactured by WAAM-CMT

Microstructure and properties research of Al-Zn-Mg-Cu alloy with high strength and high elongation fabricated by wire arc additive manufacturing

Characterization of 5356 Aluminum Walls Produced by Wire Arc Additive Manufacturing (WAAM)

Microstructure evolution and mechanical properties of wire-arc-additively manufactured Al–Cu–Mg–Ag alloy

Printing High-Strength High-Elongation Al4043 Alloy Using UNS A94043 Welding Wires through Wire Arc Additive Manufacturing

Microstructure, Hardness, and Electrical Resistivity of Al-Cu alloy fabricated via Wire Arc Additive Manufacturing

Microstructure and Mechanical Properties of an Advanced Ag-Microalloyed Aluminum Crossover Alloy Tailored for Wire-Arc Directed Energy Deposition

Evolution of microstructure and properties in 2219 aluminum alloy produced by wire arc additive manufacturing assisted by interlayer friction stir processing