Abstract:A wire arc additive manufacturing system, based on cold metal transfer technology, was utilized to manufacture the Al-Mg alloy walls. ER5556 wire was used as the filler metal to deposit Al-Mg alloys layer by layer. Based on the orthogonal experiments, the process parameters of the welding current, welding speed and gas flow, as well as interlayer residence time, were adjusted to investigate the microstructure, phase composition and crystal orientation as well as material properties of Al-Mg alloyed additive. The results show that the grain size of Al-Mg alloyed additive becomes smaller with the decrease of welding current or increased welding speed. It is easier to obtain the additive parts with better grain uniformity with the increase of gas flow or interlayer residence time. The phase composition of Al-Mg alloyed additive consists of α-Al matrix and γ (Al12Mg17) phase. The eutectic reaction occurs during the additive manufacturing process, and the liquefying film is formed on the α-Al matrix and coated on the γ phase surface. The crystal grows preferentially along the <111> and <101> orientations. When the welding current is 90 A, the welding speed is 700 mm/min, the gas flow is 22.5 L/min and the interlayer residence time is 5 min, the Al-Mg alloy additive obtains the highest tensile strength. Under the optimal process parameters, the average grain size of Al-Mg alloyed additive is 25 μm, the transverse tensile strength reaches 382 MPa, the impact absorption energy is 26 J, and the corrosion current density is 3.485 × 10−6 A·cm−2. Both tensile and impact fracture modes of Al-Mg alloyed additive are ductile fractures. From the current view, the Al-Mg alloys manufactured by WAAM-CMT have a better performance than those produced by the traditional casting process.

Printing High-Strength High-Elongation Al4043 Alloy Using UNS A94043 Welding Wires through Wire Arc Additive Manufacturing

Enhanced High-Temperature Strength and Ductility of Wire Arc Additive Manufactured Al-Ce-Mg Alloys with Fine Α-Al/al11ce3 Eutectics

Microstructure and Mechanical Properties of 304L Steel Fabricated by Arc Additive Manufacturing

Understanding the microstructural evolution and fatigue behavior of aluminum 2319 fabricated by wire arc additive manufacturing

The structure and mechanical properties of high-strength aluminum alloys fabricated with wire arc additive manufacturing

Development of a New High Strength Alloy from Low Alloy Steel Wire by Innovative Additional Cold Wire Feeding Used in Wire Arc Additive Manufacturing

Mechanical properties and microstructure characteristics of wire arc additively manufactured high-strength steels

Wire Arc Additive Manufacturing (WAAM) of Aluminum Alloy AlMg5Mn with Energy-Reduced Gas Metal Arc Welding (GMAW)

Wire arc additive manufacturing of Al-Zn-Mg-Cu alloy: Microstructures and mechanical properties

Improvement of microstructure and fatigue performance of wire-arc additive manufactured 4043 aluminum alloy assisted by interlayer friction stir processing

Microstructure Evolution and Performance of AA2024 Alloy Through Wire-Arc Additive Manufacturing Under Different Heat Inputs

Microstructure and mechanical properties of WE43 magnesium alloy fabricated by wire-arc additive manufacturing

Microstructures and Properties of Al-Mg Alloys Manufactured by WAAM-CMT

Mechanical Performance and Failure Mechanism of Layered Walls Produced by Wire Arc Additive Manufacturing in Metal Transfer Pulsed Mode

Wire arc additive manufacturing (WAAM) of nanotreated aluminum alloy 6061

Arc Additively Manufactured 5356 Aluminum Alloy with Cable-Type Welding Wire: Microstructure and Mechanical Properties

A Review of High-Strength Aluminum-Copper Alloys Fabricated by Wire Arc Additive Manufacturing: Microstructure, Properties, Defects, and Post-processing

Microstructure and mechanical properties of 600 MPa grade ultra-high strength aluminum alloy fabricated by wire-arc additive manufacturing

Wire and Arc Additive Manufacturing of High-Strength Al–Zn–Mg Aluminum Alloy

Comparative Study on Wire-Arc Additive Manufacturing and Conventional Casting of Al–Si Alloys: Porosity, Microstructure and Mechanical Property

Comparative Study on the Microstructure Evaluation of Al-Mg (Er5356) Aluminum Alloy for Aircraft Wing Stiffener Fabricated By Wire Arc Additive Manufacturing