Comparative study on the microstructures and properties of wire+arc additively manufactured 5356 aluminium alloy with argon and nitrogen as the shielding gas

Sen Li,Lin-Jie Zhang,Jie Ning,Xiang Wang,Gui-Feng Zhang,Jian-Xun Zhang,Suck-Joo Na,Bodaghi Fatemeh

DOI: https://doi.org/10.1016/j.addma.2020.101206

IF: 11

2020-08-01

Additive Manufacturing

Abstract:<p>This research explored the influences of shielding gases on the appearance of weld beads and the microstructures and mechanical properties of thin-wall samples using conventional gas metal arc welding as the heat source by using 5356 aluminium alloy welding wire as the raw materials and nitrogen (N₂) and argon (Ar) as the shielding gases. The results showed that under the same parameters and after mono-layer single-bead welding was performed using N₂ as the shielding gas, the bead height was higher, the bead width was narrower, and the penetration depth was shallower. The grain size of the thin-wall sample protected by N₂ was 43.5%–47.8% smaller than that obtained under Ar protection. However, the sample protected by N₂ contained many flaky nitrides, whose presence improved the microhardness but reduced the ultimate tensile strength (UTS) and plasticity. The average UTS of the thin-wall sample protected by N₂ in the horizontal direction was 82.5% of the UTS of the samples shielded using Ar. However, the average elongation in the horizontal direction of the samples protected by N₂ was 18.6% of that of the samples shielded by Ar. The mechanical properties of the sample protected by argon were more excellent.</p>

engineering, manufacturing,materials science, multidisciplinary