Optimization of shielding gas composition in high nitrogen stainless steel gas metal arc welding

Zeng Liu,Chenglei Fan,Zhu Ming,Chao Chen,Chunli Yang,Sanbao Lin,Langping Wang

DOI: https://doi.org/10.1016/j.jmapro.2020.08.001

IF: 5.684

2020-10-01

Journal of Manufacturing Processes

Abstract:<p>High nitrogen stainless steel has extensive applied foreground in industries. But the weldability limits the use of the steel. The weld without nitrogen can become the weakness of the joint in corrosion resistance and strength. In this study, response surface methodology was applied to optimize the Ar-N₂-CO₂ ternary shielding gas for a nitrogen-containing filler metal in high nitrogen stainless welding. The influence of the proportion of N₂ and CO₂ on the nitrogen content, the impact energy and the tensile strength were investigated by the statistical regression models. The results show that the tensile strength, nitrogen content and impact energy increase and then decrease with the increasing of CO₂, which indicates that CO₂ content should not be too high. N₂ addition can increase the nitrogen content of the weld obviously. But the impact energy decreases when N₂ content exceeds about 7%. Integrating the mathematic models of the three performances, the optimal shielding gas compositions were determined to be 87 %Ar-6.5 %N₂-6.5 %CO₂. With this optimal shielding gas, the tensile strength and impact energy reached 956.7 MPa and 166.8 J, respectively. The deviation between the experimental value and the predicted value was below 2%.</p>

engineering, manufacturing