Low-temperature Sintering and Electrical Properties of Ba0.68Sr0.32TiO3 Thick Films

Handong Yuan,Jun Liu,Mingming Gu,Shijia Feng,Ming Zhou,Ying Luo

DOI: https://doi.org/10.1016/j.ceramint.2021.02.235

IF: 5.532

2021-01-01

Ceramics International

Abstract:Ba0.68Sr0.32TiO3 (BST) thick films were prepared by screen printing on a flexible fluorophlogopite substrate. In order to realise the co-firing of the BST film with a silver electrode at a lower temperature, the BST precursor was used as a solvent for the screen-printing slurry and the cold sintering technique was used to pretreat the film. The sintering temperature of BST thick films prepared by conventional sintering process was higher than 1200 C. When sintered at 950 C, the thick films exhibited a high porosity. The density of the thick films was significantly improved after pretreatment with the cold sintering process (CSP). After the cold-sintered thick films were sintered at 950 C for 30 min and then fired with a silver electrode, the samples exhibited a relative dielectric constant of 773 (at 25 C and 10 kHz), a dielectric loss of 0.025, a remanent polarization of 5.3 mu C/cm2, and a coercive field strength of 38.1 kV/cm. Therefore, the low-temperature co-firing of BST thick films with a silver electrode was successfully realised.