Abstract:In order to overcome some problems in variable polarity gas tungsten arc welding (VP-GTAW) employed for welding aluminum alloy components, poor strength and ductility of weld metal, solidification cracking and weld porosity, a novel ultrafast-convert high frequency pulsed current VP-GTAW technique is developed. The current converting speed in the novel technique is enhanced from less than 10 A/mu s to more than 50-100 A/mu s and high frequency pulsed current which has a frequency of more than 20 kHz is exactly integrated in the positive polarity current duration. It is expected that the novel pulsed VP-GTAW technique can improve the weld quality of aluminum alloy significantly. Thus, it is imperative to understand the effect of pulsed current parameters on the weld characteristics in the pulsed VP-GTAW process. The measured results of 2219-T87 high strength aluminum alloy weld joints show that the application of ultrasonic pulse current makes the coarse grains in weld zone change to the fine equiaxed grains, and a band-like zone with finer equiaxed non-dentrites appears. The width of weld fusion zone is obviously decreased and the mechanical properties of weld joints are predominantly improved. The improvements of the structure and weld properties can be significantly enhanced with the increases of the ultrasonic pulse current amplitude and pulse frequency, and decrease of the pulse duty cycle in certain ranges. Compared with the conventional VP-GTAW, tensile strength and elongation of weld joints are increased by about 22% and 111%, respectively, under the conditions of pulse current amplitude of 100 A, pulse frequency of 40 kHz and pulse duty cycle of 20%.

Microstructure Evolutions and Properties of Al–Cu Alloy Joint in the Pulsed Power Ultrasonic-Assisted GMAW

Analysis of Droplet Transfer, Weld Formation and Microstructure in Al-Cu Alloy Bead Welding Joint with Pulsed Ultrasonic-Gmaw Method

Effect of Pulse Frequency on Weld Appearance of Al Alloy in Pulse Power Ultrasonic Assisted GMAW

Effect of Arc Behaviour and Metal Transfer Process on Aluminium Welds During Ultrasonic Frequency Pulsed GMAW

Pulsed Ultrasonic Wave Assisted GMAW of 7 A 52 Aluminum Alloy

Microstructure and mechanical properties of Q235 steel welded joint in pulsed and un-pulsed ultrasonic assisted gas tungsten arc welding

Effect of Ultrasonic Power on Microstructural and Mechanical Properties of Al/Cu Plasma Arc Welding–Brazing Joints

Microstructure and Mechanical Properties of Resistance Heat-Assisted High-Power Ultrasonic Dissimilar Welded Cu/Al Joint

Influence of Heat Input on the Appearance, Microstructure and Microhardness of Pulsed Gas Metal Arc Welded Al Alloy Weldment

Effect of ultrasonic vibration on porosity suppression and columnar-to-equiaxed transition in laser-MIG hybrid welding of aluminum alloy

Characteristics of Arc and Metal Transfer in Pulsed Ultrasonic-Assisted GMAW

Microstructure evolution and mechanical properties of Cu–Al joints by ultrasonic welding

Microstructure and Mechanical Properties of Ultrasonic Assisted Underwater Wet Welding Joints

Insight on Ultrasonic Effect of Al Cu Aluminum Alloy Joints Fabricated by Ultrasonic Assisted Non-Thinning and Penetrating Friction Stir Welding

Feasibility Analysis of Pulsed Ultrasonic for Controlling the GMAW Process and Weld Appearance

Dynamic Weld evolution during ultrasonic welding of Cu–Al joints

Influences of Ultrasonic Pulse Square-Wave Current Parameters on Microstructures and Mechanical Properties of 2219 Aluminum Alloy Weld Joints

Microstructural Evolution in Dissimilar Joint of Al Alloy and Cu During Ultrasonic Welding

Microstructure and porosity analysis in ultrasonic assisted TIG welding of 2014 aluminum alloy

Effect of Ultrasonic Pattern on Weld Appearance and Droplet Transfer in Ultrasonic Assisted MIG Welding Process

Microstructure and Mechanical Properties of Ultrasonic Welded Joint of 1060 Aluminum Alloy and T2 Pure Copper