Effect of equivalent heat input on WAAM Al-Si alloy
Chao Chen,Guorui Sun,Wenbo Du,Jiuqing Liu,Huijing Zhang
DOI: https://doi.org/10.1016/j.ijmecsci.2022.107831
IF: 7.3
2022-10-13
International Journal of Mechanical Sciences
Abstract:Heat input is a critical parameter in wire arc additive manufacturing (WAAM). A large number of studies have been carried out on the heat input of WAAM. However, the current research only focuses on the influence of different heat input values on the structure and performance of components, and the influence of equivalent heat input on the structure and performance of components is totally overlooked. In this paper, a new understanding of heat input is gained through analysis of the forming, microstructure and properties of WAAM components. Through the design of energy parameters (welding current, welding voltage, and traverse speed), three sets of the same heat input are obtained with different parameter combinations during the WAAM of aluminum-silicon alloy as the research object. The wire feeding speeds of Samples A, B, and C are 4, 6, and 8 (unit: m/min), respectively. The traverse speeds of Samples A, B, and C are 6, 11, and 16 (unit: mm/s), respectively. The results showed that the forming morphologies, microstructure and mechanical properties of thin-walled parts obtained under different parameters are significantly different with the same heat input. Under the interaction of wire feeding speed and traveling speed, the forming height of the sample decreases and the width increases, and the grain size increases with the increase of the two parameters. Sample A has the best mechanical properties, with an average tensile strength of 208.85 MPa and an average hardness of 71.66 HV. Compared with those of Sample C, the microhardness and tensile strength increased by 18.4 HV and 17.5 MPa, respectively.
engineering, mechanical,mechanics