Oxide-scale Evolution and Dynamic Oxidation Mechanism of ZrB2-SiC in High-Enthalpy Plasma Wind Tunnel

Liping Liu,Lingwei Yang,Changhao Zhao,Xueren Xiao,Zhiyong Ye,Jun Zhang,Guolin Wang,Yiguang Wang

DOI: https://doi.org/10.1016/j.jeurceramsoc.2021.02.006

IF: 5.7

2021-01-01

Journal of the European Ceramic Society

Abstract:In this work, a 1 MW Plasma wind tunnel was employed to study the dynamic oxidation mechanisms of ZrB2-SiC at heat flux ranging 0.5∼5.0 MW/m2 in reduced pressure. The results show a transition in the uppermost oxide layer from SiO2-rich glass to SiO2 when increasing heat flux from ≈0.55 and ≈1.70 MW/m2 (≈1100 °C and ≈1340 °C) to ≈2.50 MW/m2 (≈1550 °C). A temperature fluctuation was highlighted at ≈2.50 MW/m2. At higher heat flux (≥3.5 MW/m2), a ‘thermal instability’ occurred at ≈1650 °C. In addition, the ZrO2 grain structure was temperature dependent, particularly at ≈1.70 MW/m2 where the ZrO2 grain evolved from tiny grain, to equiaxed grain and to columnar grain. At higher heat flux (≥2.50 MW/m2), columnar grains were observed prior to the ‘thermal instability’. Finally, as oxidation of ZrB2-SiC was a diffusion-control process, the oxidation rate was dependent not only on temperature, but on grain structure of ZrO2.