Abstract:As a typical carbon-based material, activated carbon (AC) has satisfied adsorption performance and is of great significance in the field of volatile organic compounds (VOCs) pollutants removal. In order to further reveal the optimization mechanism of AC adsorption performance, coconut shell-based AC was selected as the research object, and different concentrations of HNO 3 coupled with microwave were used for rapid modification and activation. The characteristic changes of pore structure and surface chemical of AC before and after rapid modification were analyzed, and the performance changes of VOCs absorption were discussed from the perspective of reaction kinetics. The pore structure and surface chemical properties of before and after modification were analyzed by X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), Brunauer-Emmeta-Teller (BET) analysis, Fourier Transform Infrared Spectroscopy (FTIR), and Boehm titration. The results showed that HNO 3 coupled with microwave could significantly eliminate impurities in the pores of AC. After impregnation in HNO 3 at a concentration of 1.5 mol L −1 and under microwave irradiation of 900 W, the number of micropore on the surface of samples increased slightly. When the impregnation concentration of HNO 3 continued to increase, the two adjacent pore structures of the samples merged, which lead to a large decrease in the number of micropore and a corresponding increase in the proportion of mesoporous. Meanwhile, the specific surface area S BET of the modified NAC-6 sample increased to 1,140.40 m 2 g −1 , and the total acidic oxygen-containing functional groups on the surface increased by 0.459 mmol g −1 compared to that of the unmodified raw carbon. Furthermore, by analyzing the experimental results of formaldehyde adsorption on AC samples, it was concluded that the saturated adsorption capacity of the modified NAC-6 sample was 43% higher than that of the raw carbon. This study provides a more convenient and faster modification method for AC in the field of gas phase pollutants purification, which is helpful to realize the practical engineering application of AC with high efficiency, energy saving and sustainable.

Surface Modification of Activated Coke for NO Oxidation at Ambient Temperature

Effect of Nitric Acid Pretreatment on the Properties of Activated Carbon and Supported Palladium Catalysts

Effect of Nitrogen Doping on the Reduction of Nitric Oxide with Activated Carbon in the Presence of Oxygen

The Role of Surface Properties of Activated Carbon in the Catalytic Reduction of NO by Carbon

Nitrogen Doping of Activated Carbon Loading Fe2O3 and Activity in Carbon-Nitric Oxide Reaction

An updated study on NO catalytic oxidation over activated carbon: The effect of pore structure and a dual-site mechanism

CO2 adsorption on chemically modified activated carbon

Effect of pre-oxidation process on V2O5/AC catalyst for the selective catalytic reduction of NOx with NH3

Promotional Mechanism of La-Mn-Fe Modification on Activated Coke for NH3-SCR of NOx at Low Temperatures

Biomass and Coal Modification to Prepare Activated Coke for Desulfurization and Denitrification

Catalytic Oxidation of NO at Room Temperature by Pitch-Based Activated Carbon Fibers

Intensification of NO x Conversion over Activated Coke by Ozone Oxidation for Sintering Flue Gas at Low Temperatures

Performance optimization and kinetic analysis of HNO3 coupled with microwave rapidly modified coconut shell activated carbon for VOCs adsorption

One-step synergistic optimization of hierarchical pore topology and nitrogen dopants in activated coke for efficient catalytic oxidation of nitric oxide

Preparation of Pitch-based Activated Carbon Fibers and Their Catalytic Oxidation Performance for NO

Catalytically oxidation of NO into NO2 at room temperature by graphitized porous nanofibers

STUDY ON DENITRIFICATION PERFORMANCE OF MODIFIED ACTIVATED COKE BY METAL-OXIDES

Insight into the promotion mechanism of activated carbon on the monolithic honeycomb red mud catalyst for selective catalytic reduction of NOx

Adsorption and Reduction of NO2 over Activated Carbon at Low Temperature

Effect of Activated Carbon and Its Surface Property on the Activity of Ru/Ac Catalyst

Selective catalytic reduction of NO with NH3 over CuOX-carbonaceous materials