Effect of grain boundary segregation on dielectric properties of CaCu3Ti4O12 ceramics

Jingpeng YANG,Lingfang XU,Ruilong WANG,Haibo XIAO,Fujun YANG,V V,Changping YANG

DOI: https://doi.org/10.3969/j.issn.1000-2375.2018.01.013

2018-01-01

Abstract:The polarizability of dielectric material is sensitive to microstructures, including grain size, grain boundary and the segregationphase at grain boundary.In this work, ceramic CaCu3 Ti4 O12 was prepared by sol-gel method with a post ball milling.The influence of milling treatment on dielectric properties of CaCu3-Ti4 O12 ceramics was investigated.Experimental results indicate that the dielectric constant of CaCu3 Ti4 O12 ceramic sample is greatly affected by the ball milling.The dielectric constant of CaCu3 Ti4 O12 increases with increasing the milling time, obviously.When the milling time is 4 hours, the constant can reach a value of 106 , much higher than that of the untreated sample.The dielectric constant increases by an order of magnitude with increasing temperature by 100 K.Besides, SEM analysis indicates that the increase of the dielectric constant is related to the grain boundary segregation of CaCu3 Ti4 O12 , especially the secondary phase of CuO precipitated at grain boundaries can greatly enhance the polarization of CaCu3 Ti4 O12 by around two order of magnitude.