Abstract:Polyvinylidene fluoride (PVDF)–perfluorosulfonic acid (PFSA) blend hollow fiber ultrafiltration (UF) membranes were prepared by wet-spinning method using pure water as an external coagulation solution. Coagulation kinetics of PVDF–PFSA–DMAc system was measured by light transmittance experiment. Using PEG10000 (Mw=10,000), lysozyme (Mw=14,400), PEG20000 (Mw=20,000) and BSA (Mw=67,000), the separation performances of PVDF–PFSA blend hollow fiber UF membranes were obtained. Based on the experimental results, the delayed demixing process was observed for the dope solution M-1 without PFSA-H while the instantaneous demixing process was observed for the others with PFSA-H in the dope solutions M-2 to M-6. The precipitation rate increased with the increment of the PFSA-H concentration in PVDF–PFSA dope solution. The bore fluid solution with 95:5 DMAc:H2O resulted in single finger-like voids for PVDF–PFSA-H UF membrane. The pure water permeation flux of PVDF–PFSA-H UF membranes firstly increased from <0.1×10−5 to 119.1×10−5Lm−2h−1Pa−1 (<0.1 to 119.1Lm−2h−1bar−1) for M-1 to M-4(1) and 137×10−5Lm−2h−1Pa−1 (137Lm−2h−1bar−1) for M-4(2), and decreased from 119.1×10−5 to 79×10−5Lm−2h−1Pa−1 (119.1 to 79Lm−2h−1bar−1) for M-4(1), M-5 and M-6 as the PFSA-H concentration changed from 0% to 5% and total PVDF–PFSA-H concentration was 20wt.%. The molecular weight cut-off (MWCO) of PVDF–PFSA blend hollow fiber UF membranes spun from 20wt.% PVDF–PFSA-H concentration with 3–5wt.% PFSA-H was about 20,000 while that spun from 22wt.% PVDF–PFSA-H or PVDF–PFSA-Na concentration with 5wt.% PFSA-H or PFSA-Na was about 10,000. As the WPFSA-H/WPVDF increases from 2/18 to 5/15 for M-3–M-6, JBSA/Jw increases from 0.53 to 0.79. The anti-fouling property of PVDF–PFSA-H blend UF membrane is superior to PVDF–PFSA-Na blend membrane. Based on FTIR spectra, PFSA-H existed in PVDF–PFSA blend hollow fiber UF membranes. There is no obvious variation of the intensity of the characteristic peak at 983cm−1 assigned to C–O–C group of PFSA-H molecules. This also illustrated that PVDF–PFSA-H blend hollow fiber UF membranes were stable.

Study on the Preparation of Hollow Fiber Ultra-filtration Membrane of PSF-SPES Blend

Preparation and Performance of Polyethersulfone Hollow-Fiber Membrane

Study on the preparation of PDMS/PSF hollow fiber composite pervaporation membrane

Research and Applications of PSF Ultrafiltration Membrane

Preparation and Properties of Functionalized Carbon Nanotube/psf Blend Ultrafiltration Membranes

Preparation of Antifouling Ultrafiltration Membranes from Copolymers of Polysulfone and Zwitterionic Poly(arylene Ether Sulfone)s

Preparation of polysulfone/sulfonated polysulfone-SiO 2 nanofiltration membrane and its performance characterization

Zwitterionic Polysulfone Copolymer/Polysulfone Blended Ultrafiltration Membranes with Excellent Thermostability and Antifouling Properties

Preparation And Characterization Of Polysulfone Ultrafiltration Membrane With Peg As An Additive

Preparation of PES Hollow Fiber Composite Nanofiltration Membrane

Preparation and performance of PSf-CA hollow fiber hemodialysis blend membrane

Preparation and characterization of PVDF–PFSA blend hollow fiber UF membrane

Evaluating the Antifouling Properties of Poly(ether Sulfone)/sulfonated Poly(ether Sulfone) Blend Membranes in a Full-Size Membrane Module

Preparation and Characterization of PSf Hollow Fiber Membrane from PSf–HBPE–PEG400–NMP Dope Solution

A Facile Way to Prepare Hydrophilic Homogeneous PES Hollow Fiber Membrane Via Non-Solvent Assisted Reverse Thermally Induced Phase Separation (RTIPS) Method

Facile membrane preparation strategy to reinforce permeability of polyethersulfone (PES) micro-ultrafiltration membrane for drinking water treatment

Preparation of PDMS/PES hollow fiber composite pervaporation membrane

Morphology and Performance of Polyvinylidene Fluoride/Perfluorosulphonic Acid Hollow Fibre Ultrafiltration Blend Membranes

Fabrication of polysulfone membrane with sponge-like structure by using different non-woven fabrics

Ultrafiltration Hollow Fiber Membranes of Sulfonated Polyetherimide/polyetherimide Blends: Preparation, Morphologies and Anti-Fouling Properties

Preparation and Characterization of PVDF-PFSA Flat Sheet Ultrafiltration Membranes