Abstract:Thermoelectric devices have shown attractive application prospects with the emergence of high performance thermoelectric materials in recent years. In the Cu-Se system, bond-structure adjustment was designed to improve thermoelectric properties through simple silver doping, which induces change of phase structure, energy band structure, and thermoelectric transport nature. The polycrystalline Cu2−xAgxSe bulk samples were prepared by the spark plasma sintering (SPS) following vacuum melting and grinding. Appropriate addition of silver makes α-Cu2Se lattice expansion, and β-Cu2Se becomes the room temperature stable phase with further increase of the silver content (>=3%). Ag doping results in significant changes in valence band spectra, which improves thermoelectric transport behave in higher operation temperature. Due to the synergetic effect from electrical conductivity and Seebeck coefficient, the maximum power factor reaches 1456 μWm−1K−2 at 773 K, which increases by 10% compared with the undoped sample. It is notable that the Cu1.99Ag0.01Se bulk sample achieve an low thermal conductivity of 1.1 W m−1K−1 at 773 K, which can be attributed to enhancement of phonon scattering at different frequencies due to the diversified bond lengths and bond energy induced by Ag-doping. Benefiting from reduction of lattice thermal conductivity and enhancement of powder factor, the Cu1.99Ag0.01Se bulk sample shows the better TE transport properties and exhibits the highest ZT value ∼1.12 at 773 K.

Synthesis and Thermoelectric Properties of Cu2SnSe3-Ag Nanocomposite

Facile Synthesis of Monodisperse Cu3SbSe4 Nanoparticles and Thermoelectric Performance of Cu3SbSe4 Nanoparticle-Based Materials

Mechanisms underlying resistance to nematode infection.

Embryonal carcinoma of the pineal region

Enhanced Thermoelectric Properties of Cu2SnSe3 by (Ag,In)-Co-Doping

Synthesis of SnTe/AgSbSe 2 nanocomposite as a promising lead-free thermoelectric material

High thermoelectric performance and low thermal conductivity in Cu 2- x Na x Se bulk materials with micro-pores

Colloidal Synthesis of Cu2CdSnSe4 Nanocrystals and Hot-Pressing to Enhance the Thermoelectric Figure-of-merit.

X-linked female-sterile loci in Drosophila melanogaster.

Enhanced thermoelectric properties of Cu-Se system via bond-structure adjustment by Ag-doping

Enhancement of the Thermoelectric Performance of Cu 2 GeSe 3 via Isoelectronic (Ag, S)-co-substitution

Enhanced thermoelectric performance of AgCuTe-doped polycrystalline SnSe by lattice plainification

Low thermal conductivity and high thermoelectric performance in Cu2Se/CuAgSe composite materials

Effect of Se - site Doping on Thermoelectric Properties of Cu2SnSe3 Synthesized by Combustion

Hot-Injection Synthesis Of Cu-Doped Cu2znsnse4 Nanocrystals To Reach Thermoelectric Zt Of 0.70 At 450 Degrees C

Enhanced thermoelectric performance of Cu2SnSe3 via synergistic effects of Cd-doping and CuGaTe2 alloying

p-type Sn0.98Ag0.02Se with low thermal conductivity synthesized by hydrothermal method

Thermoelectric Properties of S and Te-doped Cu2SnSe3 Prepared by Combustion Synthesis

Polycrystalline SnSe–Sn1–vS Solid Solutions: Vacancy Engineering and Nanostructuring Leading to High Thermoelectric Performance

High thermoelectric properties realized in polycrystalline (Ag, Ga) Co-doped SnSe via two-steps point defects modulation

Ultrafast One-Step Combustion Synthesis and Thermoelectric Properties of In-doped Cu 2 SnSe 3