Abstract:As an eco-friendly thermoelectric material, Cu2SnSe3 has recently drawn much attention. However, its high electrical resistivity ρ and low thermopower S prohibit its thermoelectric performance. Herein, we show that a widened band gap and the increased density of states are achieved via S alloying, resulting in 1.6 times enhancement of S (from 170 to 277 μV/K). Moreover, doping In at the Sn site can cause a 19-fold decrease of ρ and a 2.2 times enhancement of S (at room temperature) due to both multivalence bands' participation in electrical transport and the further enhancement of the density of states effective mass, which allows a sharp increase in the power factor. As a result, PF = 9.3 μW cm–1 K–2 was achieved at ∼800 K for the Cu2Sn0.82In0.18Se2.7S0.3 sample. Besides, as large as 44% reduction of lattice thermal conductivity is obtained via intensified phonon scattering by In-doping-induced formation of multidimensional defects, such as Sn vacancies, dislocations, twin boundaries, and CuInSe2 nanoprecipitates. Consequently, a record high figure of merit of ZT = 1.51 at 858 K is acquired for Cu2Sn0.82In0.18Se2.7S0.3, which is 4.7-fold larger than that of pristine Cu2SnSe3.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.1c03120?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.1c03120</a>.Temperature dependence of Cp for Cu2SnSe3, Cu2SnSe2.7S0.3, and Cu2Sn0.82In0.18Se2.7S0.3; phase characterization for all investigated samples; temperature dependence of the ZT value for Cu2SnSe3–xSx and the repeatability of thermoelectric performance for Cu2Sn0.82In0.18Se2.7S0.3; calculation details of md*; optical band gaps for S-alloyed Cu2SnSe3; unfolded effective band structure of Cu2SnSe3; calculation of lattice thermal conductivity via the Debye–Callaway model; and the calculation details of thermopower-dependent thermoelectric properties (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c03120/suppl_file/nn1c03120_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Ultrafast One-Step Combustion Synthesis and Thermoelectric Properties of In-doped Cu 2 SnSe 3

Combustion Synthesis of Cu2snse3 Thermoelectric Materials

High Thermoelectric Performance of In-doped Cu2SnSe3 Prepared by Fast Combustion Synthesis

Direct Fabrication of Highly-Dense Cu2ZnSnSe4 Bulk Materials by Combustion Synthesis for Enhanced Thermoelectric Properties

Enhanced Thermoelectric Properties of Cu2SnSe3 by (Ag,In)-Co-Doping

Combustion Synthesis: A Rapid Way for Preparing Bulk Cu2SnSe3 Thermoelectric Materials

Effect of Se - site Doping on Thermoelectric Properties of Cu2SnSe3 Synthesized by Combustion

Facile Synthesis of Monodisperse Cu3SbSe4 Nanoparticles and Thermoelectric Performance of Cu3SbSe4 Nanoparticle-Based Materials

Co-precipitation synthesis of nanostructured Cu3SbSe4 and its Sn-doped sample with high thermoelectric performance

High thermoelectric performance of Cu3SbSe4 nanocrystals with Cu2-xSe in situ inclusions synthesized by a microwave-assisted solvothermal method

Enhanced Thermoelectric Properties of Cu2SnSe3-Based Materials with Ag2Se Addition

Boosting Thermoelectric Performance of Cu 2 SnSe 3 via Comprehensive Band Structure Regulation and Intensified Phonon Scattering by Multidimensional Defects

Thermoelectric Properties of S and Te-doped Cu2SnSe3 Prepared by Combustion Synthesis

Ultralow Thermal Conductivity and Extraordinary Thermoelectric Performance Realized in Codoped Cu3SbSe4 by Plasma Spark Sintering

Co-precipitation Synthesis of Sn And/or S Doped Nanostructured Cu3Sb1−xSnxSe4−ySy with a High Thermoelectric Performance

High Thermoelectric Performance of SnTe Via in Doping and Cu1.75Se Nanostructuring Approach

Phase Composition Manipulation and Twin Boundary Engineering Lead to Enhanced Thermoelectric Performance of Cu 2 SnS 3

Entropy and Enthalpy Co‐Tuning Strategy in Cu2‐yAgy(In0.06Sn0.94)Se2S System toward Excellent Thermoelectric Performance

Thermoelectric Performance of Cu2SnSe3-AgInSe2 Solid Solutions with Sn Vacancy

Unlocking the Potential of Cu3SbSe3: Ultralow Thermal Conductivity and Enhanced Thermoelectric Performance

Boosting Thermoelectric Performance of Cu2SnSe3 Via Comprehensive Band Structure Regulation and Intensified Phonon Scattering by Multidimensional Defects.