Abstract:ZrO2 nanocrystals were synthesised by a microwave-assisted hydrothermal method using zirconium oxychloride (ZrOCl2·8H2O), yttrium chloride (YCl3·6H2O), and liquor ammonia (NH3·H2O) as raw materials, triethanolamine (TEOA) as mineraliser, and polyethylene glycol (PEG) as dispersant. The obtained products were characterised with thermogravimetry-differential scanning calorimetry (TG-DSC), Fourier transform-infrared spectroscopy (FT-IR), X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The results show that the concentration of ZrOCl2·8H2O had little effect on the material properties, whereas the PEG molecular weight, microwave hydrothermal time and temperature, and the concentration of TEOA greatly influenced the dispersibility of the nano-sized zirconia powders. XRD and FT-IR analyses indicated that the ZrO2 nanocrystals synthesised by the microwave hydrothermal method had a tetragonal phase without any trace of monoclinic or cubic phases. The optimal parameters for preparing nano-zirconia powders with appreciable crystallinity and crystal forms included the use of PEG1000/PEG2000/PEG4000 dispersants, a microwave hydrothermal time of 30–50 min and a temperature of 200–240 °C, and a TEOA concentration of 0.3–0.5 M. Nano-ZrO2 powder prepared via our optimised microwave hydrothermal method contained mostly tetrahedral, spherically shaped, highly homogeneous, and well-dispersed 20–30 nm particles.

A New Preparation Method of Nanometer Zirconium Oxide

Preparation of Zirconia Powders by Sol-gel Process

Facile Synthesis and Characterization of ZrO₂ Nanoparticles via Modified Co-Precipitation Method

Preparation of Nano-ZrO2 powder via a microwave-assisted hydrothermal method

Study on a new, environmentally benign method and its feasibility of preparing nanometer zirconia powder

Optimization of the structure and morphology of monoclinic phase nanoscale zirconium dioxide

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

Preparation of Zirconia Base Solid Solution Nanopowder by Exothermal Solid-State Synthesis

Preparation of Magnesium Stabilized Zirconia Nanoparticles by Buffer Solution Precipitation

Preparation of ZrN Nanopowders by Internal Gelation and Carbothermic Nitridation

Hydrothermal Synthesis and Characterization of Zirconia Nanocrystallites

Preparation and Microstructure of Nanometer Tetragonal Polycrystal Zirconia Powder at Low Temperature Condition

Synthesis and Characterization of Zirconium Nitride Nanopowders by Internal Gelation and Carbothermic Nitridation

Preparation of spherical zirconia powder by nano-reactor of microemulsion and its densification behavior

Preparation and Luminescence of ZrO_2 Nanopowders Via Solvothermal Method

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature

Preparation of Nanometer Zinc Oxide Powders by Plasma Pyrolysis Technology and Their Applications.

Monoclinic zirconium oxide nanostructures synthesized by a hydrothermal route

Preparation of nano-ZnO by direct precipitation method under ultrasonic radiation and surface modification study

Synthesis and Pyrolysis Evolution of Glucose-Derived Hydrothermal Precursor for Nanosized Zirconium Carbide

Preparation of Ultrafine Powder of ZrO2-Coated Si3N4 Composites