Abstract:The microstructure evolution and mechanical properties of biodegradable Mg–3Sn–1Zn–0.5Mn alloys were investigated by the optical microscopy, X-ray diffractometer and a universal material testing machine.The corrosion and degradation behaviors were studied by potentiodynamic polarization method and immersion test in a simulated body fluid（SBF）. It was found that the as-extruded Mg–3Sn–1Zn–0.5Mn alloy has the fine equiaxed grains which underwent complete dynamic recrystallization during the hot extrusion process, with the second phase particles of Mg 2 Sn precipitated on the grain boundaries and inside the grains. The tensile strength and elongation of as-extruded Mg–3Sn–1Zn–0.5Mn alloys were 244 ± 3.7 MPa and 19.3% ± 1.7%, respectively. The potentiodynamic polarization curves in SBF solution indicated the better corrosion resistance of the as-extruded Mg–3Sn–1Zn–0.5Mn alloy in the SBF solution. Immersion test in the SBF solution for 720 h revealed that the corrosion rate of as-extruded Mg–3Sn–1Zn–0.5Mn alloy was nearly 4 ± 0.33 mm/year. The hemolysis rate of as-extruded Mg–3Sn–1Zn–0.5Mn alloy was lower than the safe value of 5% according to ISO 10993-4. As-extruded Mg–3Sn–1Zn–0.5Mn alloy showed good biocompatibility after being implanted into the dorsal muscle and the femoral shaft of the rabbit, and no abnormalities were found after short-term implantation. It was revealed that the as-extruded Mg–3Sn–1Zn–0.5Mn alloy is a promising material for biodegradable implants,which possesses an interesting combination of preferred mechanical properties, better corrosion resistance and biocompatibility.

Corrosion behavior and microstructure of biomedical Mg-Zn-Mn-Gd alloys

Effects of Microstructure Transformation on Mechanical Properties, Corrosion Behaviors of Mg-Zn-Mn-Ca Alloys in Simulated Body Fluid.

Microstructure, Mechanical Properties and Bio-Corrosion Properties of Mg-Si(-Ca, Zn) Alloy for Biomedical Application

Effect of Mn Content on Microstructure, Mechanical Properties, and Corrosion Behavior of Mg-Zn-Gd-Y Alloy

Mechanical properties and corrosion behavior of Mg-Gd-Ca-Zr alloys for medical applications

Microstructure and in vitro degradation performance of Mg-Zn-Mn alloys for biomedical application

The Influence of Gd Content on the Microstructure, Mechanical Properties, Corrosion Behavior and Corrosion Film Deposition Mechanisms of As-Extruded Mg–Zn–Mn–Sr–Gd Alloys for Biomedical Applications

Research of Dynamic Corrosion Behavior, Microstructure, and Biocompatibility of Mg–Zn–Ca–Zr Alloys in Simulated Body Fluid Solution Induced by Zn Element Addition

Structural characteristics and corrosion behavior of biodegradable Mg-Zn, Mg-Zn-Gd alloys

Corrosion Behavior in Magnesium-Based Alloys for Biomedical Applications

Enhanced Mechanical Properties and Corrosion Resistance by Minor Gd Alloying with a Hot-Extruded Mg Alloy

Alloying and Brushite Coating Improve Corrosion Resistance of Magnesium in a Simulated Physiological Environment

Investigation of Mechanical and Corrosion Properties of New Mg-Zn-Ga Amorphous Alloys for Biomedical Applications

Corrosion Products on Biomedical Magnesium Alloy Soaked in Simulated Body Fluids

Effect of Microstructure and Texture on Corrosion Resistance of Magnesium Alloy

Mechanical and Corrosion Properties of Mg-Gd-Zn-Zr-Mn Biodegradable Alloy by Hot Extrusion

Study of Microstructure and Corrosion Behavior of Cast Zn–Al–Mg Alloys

Microstructure, Mechanical Properties, Corrosion Behavior and Biocompatibility of As-Extruded Biodegradable Mg–3Sn–1Zn–0.5Mn Alloy

In vitro corrosion behavior of the extruded Mg–4Zn–1Mn alloy in different physiological solutions for biomedical applications

Effects of Zn Concentration and Heat Treatment on the Microstructure, Mechanical Properties and Corrosion Behavior of As-Extruded Mg-Zn Alloys Produced by Powder Metallurgy

A homogenous microstructural Mg-based matrix model for orthopedic application with generating uniform and smooth corrosion product layer in Ringer's solution: Study on biodegradable behavior of Mg-Zn alloys prepared by powder metallurgy as a case