Abstract:In previously reported low-fluorine MOD-YBCO studies, the lowest F/Ba mole ratio of the precursor solution was 4.5. Further lowering the F/Ba ratio would bring benefits for the environment, thick film deposition, and an understanding of the heat treatment process. On the other hand, the F/Ba ratio must be at least 2 for full conversion of the Ba-precursor to BaF2 to avoid the formation of BaCO3, which is detrimental to the superconducting performance of YBCO films. In this study, a solution with a 2:1 F/Ba mole ratio was developed, and the fluorine content of this solution was approximately only 10.3% of that used in the conventional TFA-MOD method. Attenuated total reflectance-Fourier transform-infrared spectra (ATR-FT-IR) revealed that BaCO3 was remarkably suppressed in the as-pyrolyzed film-and eliminated at 700 degrees C. Thus, YBCO films with a critical current density (J(c)) of over 5 MA cm(-2) (77 K, 0 T, 200 nm thickness) could be obtained on lanthanum aluminate single-crystal substrates. In situ FT-IR spectra showed that no obvious fluorinated gaseous by-products were detected in the pyrolysis step, which indicated that all F atoms might remain in the film as fluorides. X-ray diffraction theta/2 theta scans showed the presence of BaF2-but not of YF3 or CuF2-in films quenched at 400-800 degrees C. The formation priority of BaF2 over YF3 and CuF2 was interpreted by examining the chemical equilibrium of the potential reactions. Our study could enlarge the synthesis window of precursor solutions for MOD-YBCO fabrication, and serve as a foundation for continuously and systematically studying the influence of fluorine content in the precursor solutions.

Nucleation of YBa/sub 2/Cu/sub 3/O/sub 7/ from precursor films using the barium fluoride process

A New Direct Process to Prepare YBa2Cu3O7- films on Biaxially Textured Ag{110}<211>

Transient Liquid Assisted Nucleation Mechanism of YBa 2 Cu 3 O 7− Δ in Coated Conductor Films Derived by BaF 2 Process

Preparation of YBCO superconducting thick films On MgO substrates by modified melt growth process

Formation and Characterization of YBa2Cu3O7−δ High-Tc Thin Films by MOCVD with Single Mixed Precursor

Controlled-Growth of $\hbox{YBa}_{2}\hbox{Cu}_{3}\hbox{O}_{7-\delta} $ Film Using Modified Low-Fluorine Chemical Solution Deposition

Surface Morphology and Profile Analysis for Five-Layer YBa 2 Cu 3 O 7− Δ Thick Films Prepared by Low-Fluorine Metallorganic Deposition

In situ high temperature optical microscopy study of phase evolution in YBa 2 Cu 3 O 7 d films prepared by a fluorine-free sol – gel route

A Low-Fluorine Solution with the F/Ba Mole Ratio of 2 for the Fabrication of YBCO Films

Artificial Control for Nucleation and Growth Rate of YBa2Cu3O7-δ Coated Conductors Prepared by Low Fluorine Chemical Solution Deposition

Effect of precursor stoichiometry on the superconducting properties of fluorine-free sol–gel YBCO thin films

A Low-Fluorine Solution With A 2:1 F/Ba Mole Ratio For The Fabrication Of Ybco Films

Fabrication And Analysis Of Tri-Layer Yba2cu3 O (7-Delta) Thick Films By Low-Fluorine Mod Method

Yba2cu3o7-Delta Thin-Films with Bao Precipitates

Preparation of enhanced Jc YBCO bulks by powder melting process with a combination of submicron 211 precursor and Pt addition

Preparation of Yba2cu3o7-X Superconducting Thin-Films over Large Area Substrates

Vaporization of a mixed precursor in chemical vapor deposition of YBCO films

Fabrication and Analysis of Tri-layer YBa 2 Cu 3 O 7− δ Thick Films by Low-Fluorine MOD Method

On the thermodynamics of Barium Oxyfluoride precursor in YBCO growth via MOD process

Fabrication and Analysis of Tri-layer YBa2Cu3O7−δ Thick Films by Low-Fluorine MOD Method

Property Improvement of 600-Nm-thick YBCO Superconducting Films Fabricated Using a Pb-Modified MOD Method