Abstract:Mg-1.5Y-1.2Zn-0.44Zr alloys were newly developed as degradable metallic biomaterials. A comprehensive investigation of the microstructure, mechanical properties, in vitro degradation assessments and in vitro cytotoxicity evaluations of the as-cast state, as-heat treated state and as-extruded state alloys was done. The microstructure observations show that the Mg-1.5Y-1.2Zn-0.44Zr alloys are mainly composed of the matrix α-Mg phases and the Mg12ZnY secondary phases (LPS structure). The hot extrusion method significantly refined the grains and eliminated the defects of both as-cast and heat treated alloys and thereby contributed to the better mechanical properties and biodegradation resistance. The values of tensile strength and tensile yield strength of the alloy in the as-extruded condition are about 236 and 178 MPa respectively, with an excellent elongation of 28%. Meanwhile, the value of compressive strength is about 471 MPa and the value of bending strength is about 501 MPa. The superior bending strength further demonstrates the excellent ductility of the hot extruded alloys. The results of immersion tests and electrochemical measurements in the SBF indicate that a protective film precipitated on the alloy's surface with the extension of degradation. The protective film contains Mg(OH)2 and hydroxyapatite (HA) which can reinforce osteoblast activity and promote good biocompatibility. No significant cytotoxicity towards L-929 cells was detected and the immersion extracts of alloy samples could enhance the cell proliferation with time in the cytotoxicity evaluations, implying that the Mg-1.5Y-1.2Zn-0.44Zr alloys have the potential to be used for biomedical applications.

Mechanical and Corrosion Properties of Mg-Gd-Zn-Zr-Mn Biodegradable Alloy by Hot Extrusion

Microstructure, Mechanical Properties, Corrosion Behavior and Biocompatibility of As-Extruded Biodegradable Mg–3Sn–1Zn–0.5Mn Alloy

Effect of Extrusion on the Microstructure and Corrosion Behaviors of Biodegradable Mg–Zn–Y–Gd–Zr Alloy

Microstructure Evolution in Mg-Zn-Zr-Gd Biodegradable Alloy: the Decisive Bridge Between Extrusion Temperature and Performance

A newly developed Mg-Zn-Gd-Mn-Sr alloy for degradable implant applications: Influence of extrusion temperature on microstructure, mechanical properties and in vitro corrosion behavior

Enhanced Mechanical Properties and Corrosion Resistance by Minor Gd Alloying with a Hot-Extruded Mg Alloy

Microstructure, Mechanical Properties, and in Vitro Corrosion Behavior of Biodegradable Zn-1Fe-xMg Alloy

Gd Added Mg Alloy for Biodegradable Implant Applications

Microstructure, Mechanical Properties, in Vitro Degradation and Cytotoxicity Evaluations of Mg–1.5Y–1.2Zn–0.44Zr Alloys for Biodegradable Metallic Implants

Effects of Extrusion Ratio on Microstructure, Mechanical and Corrosion Properties of Biodegradable Mg–Nd–Zn–Zr Alloy

Micro-alloying with Mn in Zn–Mg alloy for future biodegradable metals application

Optimizing Mechanical Property and Cytocompatibility of the Biodegradable Mg-Zn-Y-Nd Alloy by Hot Extrusion and Heat Treatment

Improvement of Mechanical Properties and Corrosion Resistance of Biodegradable Mg–Nd–Zn–Zr Alloys by Double Extrusion

Research on Biodegradable Mg-Zn-Gd Alloys for Potential Orthopedic Implants: in Vitro and in Vivo Evaluations.

In Vitro and in Vivo Studies on As-Extruded Mg- 5.25Wt.%zn-0.6Wt.%ca Alloy As Biodegradable Metal

Effect of Extrusion Temperature on the Microstructure, Mechanical Properties, and in Vitro Corrosion Behavior of a Biodegradable Mg-Zn-Ca-Mn-Sn Alloy

Effects of Zn Concentration and Heat Treatment on the Microstructure, Mechanical Properties and Corrosion Behavior of As-Extruded Mg-Zn Alloys Produced by Powder Metallurgy

Effect of Mn Content on Microstructure, Mechanical Properties, and Corrosion Behavior of Mg-Zn-Gd-Y Alloy

In Vitro Study on Mg-Sn-Mn Alloy As Biodegradable Metals

Mechanical properties, corrosion, and biocompatibility of Mg-Zr-Sr-Dy alloys for biodegradable implant applications

Research on an Mg-Zn alloy as a degradable biomaterial.