Abstract:Mg-1.5Y-1.2Zn-0.44Zr alloys were newly developed as degradable metallic biomaterials. A comprehensive investigation of the microstructure, mechanical properties, in vitro degradation assessments and in vitro cytotoxicity evaluations of the as-cast state, as-heat treated state and as-extruded state alloys was done. The microstructure observations show that the Mg-1.5Y-1.2Zn-0.44Zr alloys are mainly composed of the matrix α-Mg phases and the Mg12ZnY secondary phases (LPS structure). The hot extrusion method significantly refined the grains and eliminated the defects of both as-cast and heat treated alloys and thereby contributed to the better mechanical properties and biodegradation resistance. The values of tensile strength and tensile yield strength of the alloy in the as-extruded condition are about 236 and 178 MPa respectively, with an excellent elongation of 28%. Meanwhile, the value of compressive strength is about 471 MPa and the value of bending strength is about 501 MPa. The superior bending strength further demonstrates the excellent ductility of the hot extruded alloys. The results of immersion tests and electrochemical measurements in the SBF indicate that a protective film precipitated on the alloy's surface with the extension of degradation. The protective film contains Mg(OH)2 and hydroxyapatite (HA) which can reinforce osteoblast activity and promote good biocompatibility. No significant cytotoxicity towards L-929 cells was detected and the immersion extracts of alloy samples could enhance the cell proliferation with time in the cytotoxicity evaluations, implying that the Mg-1.5Y-1.2Zn-0.44Zr alloys have the potential to be used for biomedical applications.

Research on an Mg-Zn alloy as a degradable biomaterial.

Microstructure, Mechanical Properties, in Vitro Degradation and Cytotoxicity Evaluations of Mg–1.5Y–1.2Zn–0.44Zr Alloys for Biodegradable Metallic Implants

Microstructure, Mechanical Properties, and in Vitro Corrosion Behavior of Biodegradable Zn-1Fe-xMg Alloy

Microstructure, Mechanical Properties, Corrosion Behavior and Biocompatibility of As-Extruded Biodegradable Mg–3Sn–1Zn–0.5Mn Alloy

Micro-alloying with Mn in Zn–Mg alloy for future biodegradable metals application

High-performance Mg-Zn alloy achieved by the ultrafine grain and nanoparticle design

Biocompatibility of magnesium-zinc alloy in biodegradable orthopedic implants

In Vitro and in Vivo Studies on As-Extruded Mg- 5.25Wt.%zn-0.6Wt.%ca Alloy As Biodegradable Metal

Design and characterizations of novel biodegradable Zn-Cu-Mg alloys for potential biodegradable implants

Research on Biodegradable Mg-Zn-Gd Alloys for Potential Orthopedic Implants: in Vitro and in Vivo Evaluations.

In Vitro Degradation, Hemolysis And Mc3t3-E1 Cell Adhesion Of Biodegradable Mg-Zn Alloy

Evaluation of As‐extruded Ternary Zn–Mg–Zr Alloys for Biomedical Implantation Material: in Vitro and in Vivo Behavior

Research status and future prospects of biodegradable Zn-Mg alloys

Development of biodegradable Zn-1X binary alloys with nutrient alloying elements Mg, Ca and Sr

Investigation on the preparation, microstructure, mechanical and degradation properties of laser additive manufactured Zn-Li-Mg alloy for bioresorbable application

In Vitro Study on Mg-Sn-Mn Alloy As Biodegradable Metals

Zinc Alloys for Biodegradable Medical Implants

In Vitro Degradation Performance and Biological Response of a Mg–Zn–Zr Alloy

Microstructure and in vitro degradation performance of Mg-Zn-Mn alloys for biomedical application

A novel biodegradable Mg-1Zn-0.5Sn alloy: Mechanical properties, corrosion behavior, biocompatibility, and antibacterial activity

Fabrication and Properties of Zn-3Mg-1Ti Alloy as a Potential Biodegradable Implant Material