Abstract:A Cu-0.41Mg-0.06Ca (wt.%) alloy was processed by equal channel angular pressing (ECAP) for up to 12 passes via Bc route at room temperature, and its homogeneity was evaluated from three aspects of hardness, microstructure and crystallographic texture. The hardness was measured in detail on the whole transverse planes, and the microstructure and the crystallographic texture in the central and bottom regions on the transverse planes were investigated by electron backscatter diffraction (EBSD) technique. After 1 ECAP pass, the hardness in the central region was 9.4% higher than that in the bottom region; the microstructure in the central region consisted of the elongated grains, while that in the bottom region was composed of the slightly distorted grains; the crystallographic texture in the central region followed the ideal orientations of the ECAP crystallographic texture, nevertheless the crystallographic texture in the bottom region obviously deviated from any ideal orientation of the ECAP crystallographic texture. Then, with the increase of ECAP passes, the hardness and microstructure differences between in the two regions gradually weakened, and the deviation of the crystallographic texture in the bottom region gradually decreased. After 8 ECAP passes, the both regions showed the same hardness, the similar ultrafine-grained microstructure and the similar crystallographic texture. The difference formation should be attributed to the non-uniform strain caused by the friction between the sample and the die wall, rather than caused by the corner gap. The difference weakening should be attributed to the strain hardening behavior of metals. The strength calculation showed that the Cu-Mg-Ca alloy after 8 ECAP passes had almost the same yield strengths where 593 MPa for the central region and 583 MPa for the bottom region, showing only 1.7% difference.

Influence of Friction Resistance on the Deformation of Pure Aluminum during Equal Channel Angular Extrusion Processing

Tensile and Compressive Deformation Behaviors of Commercially Pure Al Processed by Equal-Channel Angular Pressing with Different Dies

Effect of Friction on Equal Channel Angular Extrusion Process

Tensile Deformation Behaviors of CuNi Alloy Processed by Equal Channel Angular Pressing

Estimation of Friction During Equal Channel Angular (ECA) Pressing of Aluminum Alloys

Microstructure and Dry Sliding Wear Behavior of Cu–10%Al–4%Fe Alloy Produced by Equal Channel Angular Extrusion

Effect of equal channel angular extrusion process on deformation behaviors of Mg-3Al-Zn alloy

Direct Observation of Shear Deformation During Equal Channel Angular Pressing of Pure Aluminum

Deformation Behaviors of AZ31 Magnesium Alloy by Equal Channel Angular Extrusion

Finite Element Analysis for the Influence of Curvature Angle ψ of the Outside Corner on ECAE of Pure Aluminum

Annealing Behavior of Aluminium Deformed by Equal Channel Angular Pressing

Finite Element Analysis of Influence of Friction Coefficient on Equal Channel Angular Extrusion of Titanium Alloy

Severe plastic deformation of commercially pure aluminum using novel equal channel angular expansion extrusion with spherical cavity

Effects of Annealing Treatment on Mechanical and Tribological Performance of Cu–10Al–4Fe after Equal Channel Angular Extrusion

Microstructure and Mechanical Properties of Cu–10%Al–4%Fe Alloy Produced by Equal Channel Angular Extrusion

Influence of Equal Channel Angular Extrusion on the Properties of Mg-6Al Alloy

Effect of ECAE on Microstructure and Tribological Properties of Cu–10%Al–4%Fe Alloy

Influence of Equal Channel Angular Pressing and Cyclic Extrusion Compression on the Microstructure Evolution and Mechanical Properties of Pure Aluminum

Ebsp Investigation of Microstructure and Texture Evolution During Equal Channel Angular Pressing of Aluminium

EBSP Study of the Annealing Behavior of Aluminum Deformed by Equal Channel Angular Processing

Microstructure Evolution of AZ31 Mg Alloy During Equal Channel Angular Extrusion