Microstructure Evolution and Growth Behaviors of Faceted Phase in Directionally Solidified Al-Y Alloys Ii. Microstructure Evolution of Directionally Solidified Al-53%Y Peritectic Alloy
Liu Tong,Luo Liangshun,Zhang Yanning,Su Yanqing,Guo Jingjie,Fu Hengzhi
DOI: https://doi.org/10.11900/0412.1961.2015.00620
2016-01-01
Abstract:Peritectic reaction is frequently encountered in many technologically important materials (e.g., steels, brass, bronze, intermetallic compounds, magnetic materials and YBa2Cu3Ox superconductors). Many interesting microstructures have been found during directional solidification of peritectic alloys, which have drawn much attention since last decade. In this work, in order to investigate the growth behavior of Al3Y phase as a peritectic phase, directioanal solidification experiments at different pulling rates have been performed on Al-53%Y (mass fraction) peritectic alloy. The results show that the primary phase and the peritectic phase both grow continuously, the microstructure, which is parallel to the solid-liquid interface has been found and explained at a low pulling rate (V= 1 mu m/s). With the growth distance increase, the precipitating solid phase from the liquid at the quenching solid-liquid interface transforms from primary Al2Y phase to peritectic Al3Y phase. The interface consists of coarse Al3Y phase without Al2Y phase. At relatively high pulling rates, the morphologies of primary Al2Y phase transit from continuous growth to cellular phase, and further to dendrites with the pulling rate increase. The results also show that the primary phase is enclosed with the serrate peritectic phase, and Al3Y phase precipitates from the liquid in needle shape at the same time. With the growth distance further increase, Al3Y phase become thicker and more numerous. In addition, the Al3Y phase precipitated from liquid transit from needle shape to short rod and lump shape, which distributes around the peritectic structure.